摘要/Abstract

摘要： 激光同轴熔丝增材制造技术凭借其高成形柔性和材料熔化均匀等优势，为基于2系和7系铝合金的高性能异质材料整体结构的高效成形提供了新型有效解决方案。针对铝合金激光同轴熔丝增材制造过程中存在的冶金气孔缺陷问题，本研究采用实验分析与数值模拟结合的方法，分析了不同类型晶粒及晶粒不同位置处气孔分布的差异化特征，揭示了气孔析出初始特征与晶粒形核条件对组织与气孔竞协演化行为的影响机理。结果表明：205C铝合金过渡层C1等轴晶界气孔率(0.03%)显著高于晶内区域(0.01%)，7075铝合金过渡层C2柱状晶区气孔率(1.01%)与平均气孔直径(48.07 μm)分别为等轴晶区的10.1倍和1.68倍。凝固末期，柱状晶上部液相通道的气孔与下方气孔合并形成双晶界气孔，远离一次枝晶尖端的气孔被两侧柱状晶包裹形成三晶界交互气孔。多等轴晶间气孔受晶界均匀约束作用影响呈近球形形貌，柱状晶间气孔形貌受晶体取向约束呈沿晶界定向延伸的条状分布。随着柱状晶生长模式由汇聚型向平行型直至发散型转变，晶间气孔的长度、宽度和圆度逐渐增大。

关键词: 铝合金, 激光同轴熔丝增材, 微观组织, 气孔, 耦合演化

Abstract: Laser coaxial wire additive manufacturing, with its advantages of high forming flexibility and uniform material melting, offers a novel and effective solution for the efficient forming of high-performance heterogeneous material integral structures based on 2xxx and 7xxx series aluminum alloys. To address the metallurgical porosity problem during laser coaxial wire additive manufacturing of aluminum alloys, this study combines experimental analysis with numerical simulation to investigate the differential pore distribution characteristics across different grain types and locations. It further elucidates the influence mechanisms of initial pore precipitation features and grain nucleation conditions on the competitive and cooperative evolution of microstructure and porosity. The results demonstrate that in the 205C aluminum alloy transition layer C1, the porosity at equiaxed grain boundaries (0.03%) is significantly higher than that within grains (0.01%). In the 7075 aluminum alloy transition layer C2, the porosity (1.01%) and average pore diameter (48.07 μm) in the columnar grain zone are 10.1 times and 1.68 times those in the equiaxed grain zone, respectively. During the final solidification stage, pores in the upper liquid channels of columnar grains merge with underlying pores, forming double-grain-boundary pores, while pores distant from primary dendrite tips become encapsulated by adjacent columnar grains, resulting in triple-grain-boundary interactive pores. Pores between multiple equiaxed grains exhibit near-spherical morphology due to uniform grain boundary constraints, whereas those between columnar grains adopt an elongated, intergranular distribution due to crystallographic orientation constraints. As the columnar grain growth mode transitions from convergent to parallel and finally divergent, the length, width, and roundness of intergranular pores progressively increase.

Key words: aluminum alloy, laser coaxial wire additive manufacturing, microstructure, pore, coupling evolution

中图分类号:

TG156

占小红, 高转妮, 张凯昱, 王建峰, 李响, 徐方达. 205C/7075铝合金激光同轴熔丝增材制造组织与气孔耦合演化机理[J]. 机械工程学报, 2026, 62(3): 160-175.

ZHAN Xiaohong, GAO Zhuanni, ZHANG Kaiyu, WANG Jianfeng, LI Xiang, XU Fangda. The Coupling Evolution Mechanism of Microstructure and Pores during Laser Coaxial Wire Additive Manufacturing of 205C/7075 Aluminum Alloy[J]. Journal of Mechanical Engineering, 2026, 62(3): 160-175.

导出引用管理器 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

链接本文: http://www.cjmenet.com.cn/CN/10.3901/JME.260077

http://www.cjmenet.com.cn/CN/Y2026/V62/I3/160

参考文献

[1] TOLGA D，COSTAS S. Recent developments in advanced aircraft aluminum alloys[J]. Materials & Design，2014，56：862-871.
[2] 郑子樵，李劲风，陈志国，等. 铝锂合金的合金化与微观组织演化[J]. 中国有色金属学报，2011，21(10)：2337-2351. ZHENG Ziqiao，LI Jinfeng，CHEN Zhiguo，et al. Alloying and microstructural evolution of Al-Li alloys[J]. The Chinese Journal of Nonferrous Metals，2011，21(10)：2337-2351.
[3] 王磊，卢秉恒. 我国增材制造技术与产业发展研究[J]. 中国工程科学，2022，24(4)：202-211. WANG Lei，LU Bingheng. Development of additive manufacturing technology and industry in China[J]. Strategic Study of CAE，2022，24(4)：202-211.
[4] AKBARI M，KOVACEVIC R. An investigation on mechanical and microstructural properties of 316LSi parts fabricated by a robotized laser/wire direct metal deposition system[J]. Additive Manufacturing，2018，23：487-497.
[5] HOJJATZADEH S M H，PARAB N，GUO Q L，et al. Direct observation of pore formation mechanisms during LPBF additive manufacturing process and high energy density laser welding[J]. International Journal of Machine Tools and Manufacture，2020，153：103555.
[6] NILOOFAR S，ALI F. Defects in additive manufactured metals and their effect on fatigue performance：A state-of-the-art review[J]. Progress in Materials Science，2021，117：100724.
[7] GHAMARIAN I，BALL S，GHAYOOR M，et al. Statistical analysis of spatial distribution of pores in metal additive manufacturing[J]. Additive Manufacturing，2021，47：102264.
[8] FU R，TANG S Y，LU J P，et al. Hot-wire arc additive manufacturing of aluminum alloy with reduced porosity and high deposition rate[J]. Materials & Design，2021，199：109370.
[9] POUDEL A，YASIN M S，YE J F，et al. Feature-based volumetric defect classification in metal additive manufacturing[J]. Nature Communications，2022，13：6369.
[10] XU R，LI R D，YUAN T C，et al. Towards the hydrogen pore in additively manufactured AlMgScZr alloy：Influencing factors，formation kinetics mechanism[J]. Journal of Materials Science & Technology，2024，199：125-144.
[11] GU J L，GAO M J，YANG S L，et al. Pore formation and evolution in wire + arc additively manufactured 2319 Al alloy[J]. Additive Manufacturing，2019，30：100900.
[12] WEI H L，MUKHERJEE T，ZHANG W，et al. Mechanistic models for additive manufacturing of metallic components[J]. Progress in Materials Science，2020，116：100703.
[13] 吴伟，孙东科，戴挺，等. 枝晶生长和气泡形成的数值模拟[J]. 物理学报，2012，61(15)：39-47. WU Wei，SUN Dongke，DAI Ting，et al. Modeling of dendritic growth and bubble formation[J]. Acta Physica Sinica，2012，61(15)：39-47.
[14] LASKOWSKI R，AHLUWALIA R，HOCK G T W，et al. Concurrent modeling of porosity and microstructure in multilayer three-dimensional simulations of powder-bed fusion additive manufacturing of INCONEL 718[J]. Additive Manufacturing，2022，60(A)：103266.
[15] ZHANG Q Y，SUN D K，PAN S Y，et al. Microporosity formation and dendrite growth during solidification of aluminum alloys：Modeling and experiment[J]. International Journal of Heat and Mass Transfer，2020，146：118838.
[16] 朱昶胜，雷瑶，雷鹏，等. PF-LBM耦合模型下Al-Cu合金的枝晶生长和气泡形成[J]. 兰州理工大学学报，2024，50(1)：19-26. ZHU Changsheng，LEI Yao，LEI Peng，et al. Dendrite growth and bubble formation of Al-Cu alloys under PF-LBM coupling model[J]. Journal of Lanzhou University of Technology，2024，50(1)：19-26.
[17] SEYED A N，MOHSEN E，SERGIO D F，et al. Effect of bubble-induced Marangoni convection on dendritic solidification[J]. International Journal of Multiphase Flow，2019，116：137-152.
[18] HUBER G，DJURDJEVIC M B，MANSAIJEVIC S. Determination some thermo-physical and metallurgical properties of aluminum alloys using their known chemical composition[J]. International Journal of Heat and Mass Transfer，2019，139：548-553.
[19] ALIREZA A，MICHEL N，ABU S K. Solidification crack elimination in TIG welding of Al7075：Experimental investigation and modified RDG modeling[J]. Journal of Manufacturing Processes，2023，103：90-103.
[20] PHILIPPE S，CHARLES S，JOACHIM K，et al. A Scheil-Gulliver model dedicated to the solidification of steel[J]. Calphad，2015，48：184-188.
[21] GU C，RIDGEWAY C D，CINKILIC E，et al. Predicting gas and shrinkage porosity in solidification microstructure：A coupled three-dimensional cellular automaton model[J]. Journal of Materials Science & Technology，2020，49：91-105.
[22] AMBROZIAK A，KORZENIOESKI M. Using resistance spot welding for joining aluminum elements in automotive industry[J]. Archives of Civil and Mechanical Engineering，2010，10(1)：5-13.
[23] CHEN Q P，LI H X，SHEN H F. Modeling of grain structure and macrosegregation during direct chill casting of Al-Cu alloy[J]. Processes，2019，7(6)：333.
[24] DAI H J，DONG H B，ATKINSON H V，et al. Simulation of the columnar-to-equiaxed transition in alloy solidification - The effect of nucleation undercooling，density of nuclei in bulk liquid and alloy solidification range on the transition[J]. Solid State Phenomena，2008，139：129-134.
[25] YANG Z Y，JIN K N，FANG H，et al. Multi-scale simulation of solidification behavior and microstructure evolution during vacuum electron beam welding of Al-Cu alloy[J]. International Journal of Heat and Mass Transfer，2021，172：121156.
[26] LIU D H，WU D J，WANG Y S，et al. Enhanced high-temperature mechanical properties of laser-arc hybrid additive manufacturing of Al-Zn-Mg-Cu alloy via microstructure control[J]. Journal of Materials Science & Technology，2024，169：220-234.
[27] ZHU M，LI Z，AN D，et al. Cellular automaton modeling of microporosity formation during solidification of aluminum alloys[J]. ISIJ International，2014，54(2)：384-391.
[28] DONG H B，LEE P D. Simulation of the columnar-to-equiaxed transition in directionally solidified Al-Cu alloys[J]. Acta Materialia，2005，53(3)：659-668.
[29] LEE P D，HUNT J D. Hydrogen porosity in directional solidified aluminium-copper alloys：In situ observation[J]. Acta Materialia，1997，45(10)：4155-4169.
[30] ATWOOD R C，SRIDHAR S，ZHANG W，et al. Diffusion-controlled growth of hydrogen pores in aluminum-silicon castings：In situ observation and modeling [J]. Acta Materialia，2000，48(2)：405-417.