大压下量限宽轧制AZ31镁合金板材的边裂行为及强化机制

doi:10.3901/JME.2021.08.146

摘要/Abstract

摘要： AZ31镁合金板在航空、航天、汽车、电子、武器等轻量化领域具有广阔的应用前景，但其塑性成形能力较差，无法承受单道次大压下量轧制变形，且易产生边裂。对AZ31镁合金板分别进行传统轧制和限宽轧制，结果表明，采用限宽轧制时，镁合金板材的单道次实际压下量最高可达50%，双向压缩应力状态可有效抑制边裂产生，裂纹长度在2 mm以内；同等压下量时，传统轧制的镁合金板边裂严重，中心区域也出现鱼鳞状裂纹。与原始板材相比，限宽轧制镁合金板的位错强化作用明显，沿轧向的屈服强度和抗拉强度分别提高了54.7%和54.1%，沿横向的屈服强度和抗拉强度分别提高了383.9%和131.1%。限宽轧制板材沿横向的强度和伸长率均高于轧向，主要原因是沿横向的细晶强化作用更强。

关键词: AZ31镁合金板, 限宽轧制, 大压下量, 边裂, 强化

Abstract: AZ31 magnesium alloy sheet has a broad application prospect in the field of lightweight including aviation, aerospace, automotive, electronics, weapons, etc. However, its plastic forming ability is so poor that it cannot withstand large rolling reduction in a single pass and easy to produce edge cracks. Traditional rolling and width-limited rolling are conducted on AZ31 sheet respectively. The results show that the actual maximum single rolling reduction can reach 50% and the length of edge crack is less than 2 mm under bidirectional compressive stress. However, serious edge cracks and fish-scale cracks in center region can be observed in AZ31 sheet fabricated by traditional rolling with 50% rolling reduction. Compared with as-received sheet, the strengthening mechanism of the width-limited rolled magnesium sheet is mainly dislocation strengthening. The yield strength and tensile strength of width-limited rolled sheet along the rolling direction increase by 54.7% and 54.1%, and along the transverse direction increase by 383.9% and 131.1%, respectively. The strength and elongation along the transverse direction of width-limited rolled sheet are higher than that along the rolling direction owing to its stronger refinement strengthening effect.

Key words: AZ31 magnesium alloy sheet, width-limited rolling, large rolling reduction, edge crack, strengthening

中图分类号:

TG33

聂慧慧, 郑留伟, 田静, 梁伟. 大压下量限宽轧制AZ31镁合金板材的边裂行为及强化机制[J]. 机械工程学报, 2021, 57(8): 146-153.

NIE Huihui, ZHENG Liuwei, TIAN Jing, LIANG Wei. Edge Crack Behavior and Strengthening Mechanism of Width-limited Rolled AZ31 Magnesium Sheet with Large Reduction[J]. Journal of Mechanical Engineering, 2021, 57(8): 146-153.

导出引用管理器 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

链接本文: http://www.cjmenet.com.cn/CN/10.3901/JME.2021.08.146

http://www.cjmenet.com.cn/CN/Y2021/V57/I8/146

参考文献

[1] 莫华均，程仁山，马立峰，等. 大应变轧制Mg-Al-Sn合金板材的微观组织与力学性能[J]. 机械工程学报，2020，56(2)：56-62. MO Huajun，CHENG Renshan，MA Lifeng，et al. Microstructure and mechanical properties of Mg-Al-Sn alloy sheet produced by large strain rolling[J]. Journal of Mechanical Engineering，2020，56(2)：56-62.
[2] 李落星，周佳，张辉. 车身用铝、镁合金先进挤压成形技术及应用[J]. 机械工程学报，2012，48(18)：35-43. LI Luoxing，ZHOU Jia，ZHANG Hui. Advanced extrusion technology and application of aluminium，magnesium alloy for vehicle body[J]. Journal of Mechanical Engineering，2012，48(18)：35-43.
[3] 蒋成钢，陈章华，臧勇. 镁合金板材温热冲压过程的各向异性损伤与失效分析[J]. 机械工程学报，2013，49(16)：62-69. JIANG Chenggang，CHEN Zhanghua，ZANG Yong. Anisotropic damage and failure analysis of magnesium alloy sheet thermal stamping[J]. Journal of Mechanical Engineering，2013，49(16)：62-69.
[4] SHI Yansong，SHU Qinghai，ZHAO Shuai，et al. Effect of controlled rolling temperature on microstructure and properties of Mg-9Li-1Zn alloy sheet[J]. Journal of Alloy and Compounds，2020，835：55296.
[5] ZHI Chenchen，MA Lifeng，HUANG Qingxue，et al. Improvement of magnesium alloy edge cracks by multi-cross rolling[J]. Journal of Materials Processing Technology，2017，255：333-339.
[6] CULBERTSON D，JIANG Yanyao. An experimental study of the orientation effect on fatigue crack propagation in rolled AZ31B magnesium alloy[J]. Materials Science &; Engineering A，2016，676：10-19.
[7] 徐海洁，马立峰，刘崇林，等. AZ31B镁合金板材多道次轧制路径研究[J]. 机械工程学报，2017，53(10)：43-51. XU Haijie，MA Lifeng，LIU Chonglin，et al. Research of multi-pass rolling routes for AZ31B Magnesium alloy sheet[J]. Journal of Mechanical Engineering，2017，53(10)：43-51.
[8] WU Jialin，JIN Li，DONG Jie，et al. The texture and its optimization in magnesium alloy[J]. Journal of Materials Science &; Technology，2020，42(7)：177-191.
[9] XIA Weijun，CHEN Zhenhua，CHEN Ding，et al. Microstructure and mechanical properties of AZ31 magnesium alloy sheets produced by differential speed rolling[J]. Journal of Materials Processing Technology，2009，209(1)：26-31.
[10] KIM W J，LEE J B，KIM W Y，et al. Microstructure and mechanical properties of Mg-A-Zn alloy sheets severely deformed by asymmetrical rolling[J]. Scripta Materialia，2007，56：309-312.
[11] 谭湘夫，毛大恒，蔡安辉，等. 镁合金板带双辊连续铸轧试验研究[J]. 机械工程学报，2012，48(16)：30-35. TAN Xiangfu，MAO Daheng，CAI Anhui，et al. Experimental study on twin-roll casting magnesium alloy strip[J]. Journal of Mechanical Engineering，2012，48(16)：30-35.
[12] WANG Pan，ZHOU Bo，YAO Hongxiang，et al. Aberrant intra- and inter-network connectivity architectures in Alzheimer’s disease and mild cognitive impairment[J]. Scientific Reports，2015，5(6)：1-12.
[13] KIM S J，KIM D Y，KIM Y S，et al. Influence of constraint condition on rolling behavior of magnesium alloy at low temperatures[J]. Metals and Materials International，2015，21(4)：719-725.
[14] HUANG Zhiquan，HUANG Qingxue，WEI Jianchun，et al. Inhibitory effects of prefabricated crown on edge crack of rolled AZ31magnesium alloy plate[J]. Journal of Materials Processing Technology，2017，246：85-92.
[15] ZHANG Dingfei，DAI Qingwei，FANG Lin，et al. Prediction of edge cracks and plastic-damage analysis of Mg alloy sheet in rolling[J]. Transactions of Nonferrous Metals Society of China，2011，21(5)：1112-1117.
[16] 马立峰，贾伟涛，林金保，等. 铸态AZ31B镁合金变温轧制本构数学模型的建立[J]. 稀有金属材料与工程，2016，45(2)：339-345. MA Lifeng，JIA Weitao，LIN Jinbao，et al. Establishment of a constitutive model of temperature-changed rolling process for as-cast AZ31B magnesium alloy[J]. Rare Metal Materials and Engineering，2016，45(2)：339-345.
[17] PEKGULERYUZ M，CELIKIN M，HOSEINI M，et al. Study on edge cracking and texture evolution during 150℃ rolling of magnesium alloys：The effects of axial ratio and grain size[J]. Journal of Alloys and Compounds，2012，510：15-25.
[18] KWEON S. Damage in edge cracking of rolled metal slabs[J]. Mechanics Research Communications，2015，63：13-20.
[19] 韦建春，黄庆学，黄志权，等. 变厚度轧制对AZ31镁合金板材边部损伤影响分析[J]. 稀有金属材料与工程，2018，47(2)：652-656. WEI Jianchun，HUANG Qingxue，HUANG Zhiquan，et al. Variable gauge rolling impact on the edge damage of AZ31 magnesium alloy sheets[J]. Rare Metal Materials and Engineering，2018，47(2)：652-656.
[20] MANABE S，UTSUNOMIYA H，SAKAI T，et al. Morphology of edge cracks of rolled magnesium alloy sheet[J]. Advanced Materials Research，2014，922：469-474.
[21] 李洋，马立峰，姜正义，等. 通过流固耦合加热的轧辊温度场分析[J]. 机械工程学报，2018，54(24)：51-60. LI Yang，MA Lifeng，JIANG Zhengyi，et al. Temperature field analysis of roll heated by fluid-solid coupled heat transfer[J]. Journal of Mechanical Engineering，2018，54(24)：51-60.
[22] NISHIMURA K，MIYAZAKI N. Molecular dynamics simulation of crack growth under cyclic loading[J]. Computational Materials Science，2004，31(3-4)：269-278.
[23] GUO Fei，ZHANG Dingfei，YANG Xusheng，et al. Influence of rolling speed on microstructure and mechanical properties of AZ31 Mg alloy rolled by large strain hot rolling [J]. Materials Science and Engineering：A，2014，607，383-389.
[24] 刘筱，朱必武，吴远志，等. 中高应变速率轧制AZ31镁合金的边裂、组织与性能[J]. 中国有色金属学报，2019，29(2)：232-240. LIU Xiao，ZHU Biwu，WU Yuanzhi，et al. Edge crack，microstructure and mechanical property of AZ31 magnesium alloy sheets rolled by medium-high strain rate[J]. The Chinese Journal of Nonferrous Metals，2019，29(2)：232-240.
[25] MAO Longhui，LIU Chuming，GAO Yonghao，et al. Microstructure and mechanical anisotropy of the hot rolled Mg-8.1Al-0.7Zn-0.15Ag alloy[J]. Materials Science &; Engineering A，2017，701：7-15.
[26] 刘庆. 镁合金塑性变形机理研究进展[J]. 金属学报，2010，46(11)：1458-1472. LIU Qing. Research progress on plastic deformation mechanism of Mg alloys[J]. Acta Metallurgica Sinica，2010，46(11)：1458-1472.
[27] WEI Jiansheng，JIANG Shunong，CHEN Zhiyong，et al. Increasing strength and ductility of a Mg-9Al alloy by dynamic precipitation assisted grain refinement during multi-directional forging[J]. Materials Science &; Engineering A，2020，780：139192.
[28] ZHENG Ruixiao，DU Junping，GAO Si，et al. Transition of dominant deformation mode in bulk polycrystalline pure Mg by ultra-grain refinement down to sub-micrometer[J]. Acta Materialia，2020，198：35-46.
[29] WANG S C，ZHU Z，STARINK M J. Estimation of dislocation densities in cold rolled Al-Mg-Cu-Mn alloys by combination of yield strength data，EBSD and strength models[J]. Journal of Microscopy，2005，217：174-178.
[30] YAO Y，HUANG Z H，MA H，et al. High strength Mg-1.4Gd-1.2Y-0.4Zn sheet and its strengthening mechanisms[J]. Materials Science &; Engineering A，2019，747：17-26.
[31] BHATTACHARYYA J J，WANG F，WU P D，et al. Demonstration of alloying，thermal activation，and latent hardening effects on quasi-static and dynamic polycrystal plasticity of Mg alloy WE43-T5 plate[J]. International Journal of Plasticity，2016，81：123-151.
[32] BETTLES C，BARNETT M. Advances in wrought magnesium alloys：Fundamental of processing，properties and applications[M]. Oxford：Woodhead Publishing，2012.
[33] TAN J C，TAN M J. Dynamic continuous recrystallization characteristics in two stage deformation of Mg-3Al-1Zn alloy sheet[J]. Materials Science &; Engineering A，2003，339(1)：124-132.
[34] 杨平. 电子背散射衍射技术及其应用[M]. 北京：冶金工业出版社，2013. YANG Ping. Electron backscattering diffraction technique and its application[M]. Beijing：Metallurgical Industry Press，2013.
[35] 张士宏，宋广胜，宋鸿武，等. 镁合金板材温热变形机理及温热成形技术[J]. 机械工程学报，2012，48(18)：28-34. ZHANG Shihong，SONG Guangsheng，SONG Hongwu，et al. Deformation mechanism and warm forming technology for magnesium alloys sheets[J]. Journal of Mechanical Engineering，2012，48(18)：28-34.