热压Ni-MoS2自润滑复合材料在不同温度的往复摩擦磨损特性

汪复兴;吴运新;程荫芊;陈南平;黄菊生;李立军   

  1. 清华大学
  • 发布日期:1995-07-01

FRICTION AND WEAR BEHAVIOURS OF HOT-PRESSED Ni-MOS2 SELF-LUBRICATING COMPOSITES IN RECIPROCATING SLIDING AT DIFFERENT TEMPERATURES

Wang Fuxing;Wu Yunxin;Cheng Yinqian;Chen Nanping;Huang Jiusheng;Li Lijun   

  1. Qinghua University
  • Published:1995-07-01

摘要: 采用自润滑复合材料,对提高某些机械摩擦副的使用寿命有很显著的效果。研究了热压Ni-MoS2自润滑复合材料与GCr15钢球组成的点接触配对副,在室温和高温条件下进行微幅往复摩擦运动时的自润滑特性。考察了载荷、温度及MoS2含量对摩擦系数和磨损率的影响,并借助扫描电镜观察磨损表面的形貌特征。结果表明:摩擦系数随载荷增加而不断提高;温度在400℃以下时,摩擦系数能保持较低数值;在室温和250℃时,含60%MoS2的复合材料均具有最低磨损率;提高MoS2含量有助于改善高温自润滑性;MoS2转移润滑膜的完整程度可作为Ni-MoS2复合材料自润滑性能好坏的判据。

关键词: 二硫化钼, 复合材料, 固体润滑剂, 摩擦磨损, 自润滑

Abstract: Self-lubricating composites are very effective for increasing the service life of friction pairs in some machines. This paper deals with the self-lubricating properties of hot-pressed Ni-MoS2 composites in air at room temperature and elevated temperatures, when they are frictionally coupled with reciprocating sliding ball of GCrl5 bearing steel. The effects of load, temperature and MOS2 content on friction coefficient and wear rate have been investigated respectively. The morphologies of wear tracks have been examined under scanning electron microscope (SEM). The results show that the friction coefficient increases continuously with the increasing of load, and can be kept at lower level until the temperature is elevated to 400℃: the composite containing 60% MoS2 possesses the lowest wear rate at both room temperature and 250℃. The increase of MoS2 content is beneficial to improving the high temperature self-lubricating property of the composites. It is suggested that the homogenity and integrity of MoS2 transfer film formed on the frictional surfaces can be as the evaluation criterion of the self-lubricating property of Ni-MoS2 composites.

Key words: Composite, Molybdenum disulfide, Self-lubrication, Solid lubricant Friction, Wear