高能离子源清洗对AlCrN刀具涂层结构及性能的影响

doi:10.3901/JME.2017.24.034

机械工程学报 ›› 2017, Vol. 53 ›› Issue (24): 34-41.doi: 10.3901/JME.2017.24.034

• 特邀专栏：表面工程先进技术及其服役行为（上） • 上一篇下一篇

扫码分享

高能离子源清洗对AlCrN刀具涂层结构及性能的影响

张世宏^1,2, 毛陶杰^1,2, 方炜^1,2, 蔡飞², 王启民^2,3, 张腾飞²

1. 安徽工业大学材料科学与工程学院马鞍山 243002;
2. 安徽工业大学现代表界面工程研究中心马鞍山 243002;
3. 广东工业大学机电工程学院广州 510006

收稿日期:2017-03-27 修回日期:2017-07-19 发布日期:2017-12-20
通讯作者: 张世宏(通信作者),男,1981年出生,博士,教授,博士研究生导师。主要研究方向为刀具涂层和刀具切削。E-mail:tougaoyouxiang206@163.com
基金资助:
国家自然科学基金（51305002，51275095，51522502）和安徽省自然科学基金（1408085QE92）资助项目。

Effects of High-energy Ion Source Cleaning Technology on the Microstructure and Mechanical Properties of AlCrN Coatings

ZHANG Shihong^1,2, MAO Taojie^1,2, FANG Wei^1,2, CAI Fei², WANG Qimin^2,3, ZHANG Tengfei²

1. School of Material Science and Engineering, Anhui University of Technology, Maanshan 243002;
2. Research Center of Modern Surface and Interface Engineering, Anhui University of Technology, Maanshan 243002;
3. School of Electro-mechanical Engineering, Guangdong University of Technology, Guangzhou 510006

Received:2017-03-27 Revised:2017-07-19 Published:2017-12-20

摘要/Abstract

摘要： 采用自主研发的离子源增强多弧离子镀设备，研究涂层沉积前不同清洗工艺对基材表面粗糙度以及所制备的AlCrN涂层的表面形貌、硬度、膜基结合力、摩擦磨损和切削性能的影响。研究结果表明，高能Ar⁺清洗可以更有效清洁基材表面。与传统弧源清洗技术相比，经高能离子源清洗后的基体表面粗糙度降低，沉积态涂层的表面粗糙度更低。相比于传统弧源清洗工艺，高能Ar⁺清洗可以显著提高膜基结合强度，达到48.7 N，摩擦因数和磨损率均降低，涂层刀具寿命提高了3倍。

关键词: AlCrN涂层, 离子源清洗, 磨损, 切削

Abstract: Ion source enhanced cleaning technology has been used before coating deposition due to its significant contribution to improve the properties of coatings. High-energy Ar⁺ ion cleaning source is used. The surface roughness of the substrates is characterized after utilizing various ion cleaning conditions before deposition. The microstructure, surface morphology, hardness, adhesion strength, friction and wear properties of the AlCrN coatings deposite on each ion-cleaned surface are systematically investigated. The results show that these high-energy Ar⁺ ions more effectively clean the surface of the workpieces with low bias voltage and significantly improve the adhesion strength of the coatings up to 48.7 N, which is much higher than that of the coatings fabricated through traditional cleaning techniques, and the wear and friction coefficient also decreases. In addition, after high-energy Ar⁺ ions, the coated tool life is also increased by 3 times in high-speed cutting tests.

Key words: AlCrN coating, cutting performance, ion source cleaning, wear

中图分类号:

TG156

张世宏, 毛陶杰, 方炜, 蔡飞, 王启民, 张腾飞. 高能离子源清洗对AlCrN刀具涂层结构及性能的影响[J]. 机械工程学报, 2017, 53(24): 34-41.

ZHANG Shihong, MAO Taojie, FANG Wei, CAI Fei, WANG Qimin, ZHANG Tengfei. Effects of High-energy Ion Source Cleaning Technology on the Microstructure and Mechanical Properties of AlCrN Coatings[J]. Journal of Mechanical Engineering, 2017, 53(24): 34-41.

参考文献

[1] 郑康培,刘平,李伟,等. AlCrN硬质涂层材料的研究进展[J]. 材料导报,2010,24(9):44-48. ZHENG Kangpei,LIU Ping,LI Wei,et al. Progress in research of AlCrN hard coating materials[J]. Materials Review,2010,24(9):44-48.
[2] SOKOVIC M. Quality management in development of hard coatings on cutting tools[J]. Achiev. Mater. Manuf. Eng.,2007,24(1):421.
[3] DOBRZANSKI L A,LUKASZKOWICZ K,LABISZ K. Structure,texture and chemical composition of coatings deposited by PVD techniques[J]. Arch. Materials Science and Engineering,2009,37(1):45.
[4] 吴凤芳. PVD氮化物涂层的冲蚀磨损特性及机理的研究[D]. 济南:山东大学,2011. WU Fengfang. Erosion wear performance and mechanism of PVD nitride coatings[D]. Jinan:Shangdong University,2011.
[5] YANG S,LI X,TEER D G. Properties and performance of CrTiAlN multilayer hard coatings deposited using magnetron sputtering plating[J]. Surface Engineering,2002,18(5):391-396.
[6] COOKE K E,BAMBER M,BASSAS J,et al. Multilayer nitride coatings by closed field unbalanced magnetron sputtering plating[J]. Surface and Coatings Technology,2003,162(2-3):276-287.
[7] SOUZA J V C. Development and characterization of Si₃N₄ coated AlCrN ceramic cutting tool[J]. Materials Science Forum,2010,660-661:697-700.
[8] CHANDIRAN A,ANANDAN N,SAKTHIVEL S. Comparative study on tool life and wear resistance of titanium nitride (TiN) and aluminium chromium nitride (AlCrN) coated carbide inserts[J]. Tribology-Materials Surfaces & Interfaces,2012(4):160-167.
[9] 姜雪峰,刘清才,王海波. 多弧离子镀技术及其应用[J]. 重庆大学学报,2006,29(10):55-58. JIANG Xuefeng,LIU Qingcai,WANG Haibo. Technology and application of multi-arc ion plating[J]. Journal of Chongqing University,2006,29(10):55-58.
[10] FOX-RABINOVICH G,VELDHUIS S C,KOVALEV A I,et al. Features of self-organization in ion modified nanocrystalline plasma vapor deposited AlTiN coatings under severe tribological conditions[J]. Journal of Applied Physics,2007,102(7):074305-074305-13.
[11] CAI Y,WANG R Y,LIU H D,et al. Investigation of (Ti:N)-DLC coatings prepared by ion source assisted cathodic arc ion-plating with varying Ti target currents[J]. Diamond & Related Materials,2016,69:183-190.
[12] 孔德军,付贵忠,王文昌,等. 阴极离子镀AlCrN涂层化学元素面扫描与线扫描分析[J]. 真空科学与技术学报,2014,34(3):235-240. KONG Dejun,FU Guizhong,WANG Wenchang,et al. High temperature mechanical behaviors of AlCrN coatings grown by cathodic arc ion plating[J]. Chinese Journal of Vacuum Science and Technology,2014,34(3):235-240.
[13] GALINDO R E,ENDRINO J L,MARTINEZ R,et al. Improving the oxidation resistance of AlCrN coatings by tailoring chromium out-diffusion[J]. Spectrochimica Acta Part B Atomic Spectroscopy,2010,65(11):950-958.
[14] WILLMANN H,MAYRHOFER P H,PERSSON P O A,et al. Thermal stability of Al-Cr-N hard coatings[J]. Scripta Materialia,2006,54(11):1847-1851.
[15] COL M,KIR D,ERESIR E. Wear and blanking performance of AlCrN PVD-coated punches[J]. Materials Science,2013,48(4):514-520.
[16] CHO I S,AMANOV A,KIM J D. The effects of AlCrN coating,surface modification and their combination on the tribological properties of high speed steel under dry conditions[J]. Tribology International,2015,81:61-72.
[17] 宋贵宏,杜昊,贺春林. 硬质与超硬涂层:结构,性能,制备与表征[M]. 北京:化学工业出版社,2007. SONG Guihong,DU Hao,HE Chunlin. Hard and super hard coatings:structure,properties,preparation and characterization[M]. Beijing:Chemical Industry Press,2007.
[18] CHEN Mohan,WU Dongqing,CHEN Wanglin,et al. Structural optimisation and electrochemical behaviour of AlCrN coatings[J]. Thin Solid Films,2016,612:400-406.
[19] 郑洁. 离子氮碳共渗-AlCrN复合涂层制备工艺及力学性能研究[D]. 马鞍山:安徽工业大学,2016. ZHEN Jie. Fabrication and mechanical property research of ion carbonitriding-AlCrN composite coatings[D]. Maanshan:Anhui University of Technology,2016.

高能离子源清洗对AlCrN刀具涂层结构及性能的影响

Effects of High-energy Ion Source Cleaning Technology on the Microstructure and Mechanical Properties of AlCrN Coatings

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	殷振, 张坤, 戴晨伟, 程敬彩, 徐海龙, 李华. 超声椭圆振动磨削SiC陶瓷的砂轮磨损与磨削性能研究[J]. 机械工程学报, 2024, 60(9): 57-74.
[2]	郑开魁, 赵信哲, 牟刚, 任志英. 超声波滚压强化TC11钛合金的表面质量与摩擦磨损性能[J]. 机械工程学报, 2024, 60(9): 137-151.
[3]	李继成, 陈广俊, 许金凯, 于化东. C/SiC复合材料激光超声复合微切削材料损伤机理与表面质量研究[J]. 机械工程学报, 2024, 60(9): 189-205.
[4]	王晓铭, 李长河, 杨敏, 张彦彬, 刘明政, 高腾, 崔歆, 王大中, 曹华军, 陈云, 刘波. 纳米生物润滑剂微量润滑加工物理机制研究进展[J]. 机械工程学报, 2024, 60(9): 286-322.
[5]	刘水清, 付锦园, 沈骁, 韩旭. 点胶机器人撞针磨损建模与不确定性分析[J]. 机械工程学报, 2024, 60(7): 34-44.
[6]	陈守安, 肖科, 程功, 韩彦峰. 混合润滑下考虑表面形貌的齿面摩擦与接触特性[J]. 机械工程学报, 2024, 60(7): 184-194.
[7]	蒋鑫池, 卢纯, 莫继良, 陈孝婷, 张庆贺, 赵婧. 考虑磨损率随温度变化的列车制动摩擦块高温磨损仿真分析[J]. 机械工程学报, 2024, 60(7): 195-202.
[8]	刘安南, 刘战强, 蔡士祥, 赵金富, 王兵. 切削加工车削刀具断屑装置及技术研究综述[J]. 机械工程学报, 2024, 60(7): 334-349.
[9]	魏永峭, 张晋, 王少江, 漆小虎, 郭瑞, 杨海江. 变双曲圆弧齿线圆柱齿轮传动界面磨损规律及敏感性分析[J]. 机械工程学报, 2024, 60(5): 81-94.
[10]	杨树财, 韩佩, 佟欣, 刘献礼, 张晓辉. 刀具介观几何特征成形技术及其作用研究[J]. 机械工程学报, 2024, 60(5): 317-351.
[11]	贾康, 王浩, 任东旭, 洪军. 一种圆柱型车齿刀的安装模型及无干涉设计方法[J]. 机械工程学报, 2024, 60(5): 352-361.
[12]	冯勇, 周豪杰, 周智远, 贾晓林, 秦育彦, 徐伟伟. 低频扭转振动辅助螺旋铣孔切削力模型研究[J]. 机械工程学报, 2024, 60(5): 390-402.
[13]	王丹丹, 黄伟迪, 张军辉, 赵守军, 于斌, 刘施镐, 吕飞, 苏琦, 徐兵. 基于边缘计算的轴向柱塞泵磨损状态辨识方法研究[J]. 机械工程学报, 2024, 60(4): 189-199.
[14]	纪佳馨, 彭程, 项冲, 黄乐, 郭飞. 考虑变速条件的斯特封磨损寿命预测方法[J]. 机械工程学报, 2024, 60(3): 191-202.
[15]	何春雷, 王姝淇, 李东洋, 耿昆, 陈光, 任成祖. 晶粒对多晶材料超精密切削影响的研究进展[J]. 机械工程学报, 2024, 60(3): 373-392.