冲击和非冲击疲劳载荷下裂纹扩展的研究

于杰;金志浩;涂铭旌;周惠久

西安交通大学

发布日期:1990-03-01

STUDY ON CRACK PROPAGATION IN IMPACT FATIGUE AND NON-IMPACT FATIGUE

Yu Jie;Jin Zhihao;Tu Mingjing;Zhou Huijiu

Xi'an Jiaotong University

Published:1990-03-01

摘要/Abstract

摘要： 对几种典型材料分别进行了四点弯曲冲击和非冲击疲劳裂纹扩展试验。结果表明，相同ΔK条件下，冲击和非冲击疲劳裂纹扩展速率之间存在三种类型的关系，这三种类型的关系与材料在两种载荷制度作用下的微观断裂机制紧密相联，统一了过去在冲击和非冲击疲劳裂纹扩展对比试验中的矛盾结果。

关键词: 冲击疲劳和非冲击疲劳, 裂纹扩展速率

Abstract: Crack propagation in 4-point bending impact fatigue and non-impact fatigue tests were studied using a few typical alloys. It has been found that there are three different types of relations between crack propagation in impact fatigue and that in non-impact fatigue. These relations are strongly associated with the micro-fracture mechanisms under impact and non-impact fatigue loads. The contradictory test results ottained by different authors in the past on the comparative study of crack propagation in impact fatigue and non-impact fatigue can thus be unified.

Key words: 冲击疲劳和非冲击疲劳, 裂纹扩展速率

于杰;金志浩;涂铭旌;周惠久. 冲击和非冲击疲劳载荷下裂纹扩展的研究[J]. , 1990, 26(2): 14-18.

Yu Jie;Jin Zhihao;Tu Mingjing;Zhou Huijiu. STUDY ON CRACK PROPAGATION IN IMPACT FATIGUE AND NON-IMPACT FATIGUE[J]. , 1990, 26(2): 14-18.

[1]	施祎, 杨晓光, 杨迪迪, 苗国磊, 石多奇. 定向凝固镍基高温合金DZ125疲劳裂纹扩展速率研究[J]. 机械工程学报, 2019, 55(13): 45-52.
[2]	樊俊铃, 郭杏林. 弹塑性疲劳裂纹扩展行为的数值模拟[J]. 机械工程学报, 2015, 51(10): 33-40.
[3]	姚志浩;董建新;张麦仓;郑磊. 组织特征对粉末高温合金FGH96疲劳裂纹扩展速率的影响[J]. , 2013, 49(20): 158-164.
[4]	丁振宇;高增梁;王效贵. 16MnR钢过载峰作用下的疲劳裂纹扩展行为研究[J]. , 2013, 49(16): 84-90.
[5]	陈龙;蔡力勋. 考虑裂尖疲劳损伤的材料疲劳裂纹扩展行为研究[J]. , 2012, 48(20): 51-56.
[6]	王璞;董建新;韩一纯;杨;亮. 组织特征对GH864合金裂纹扩展行为的影响[J]. , 2009, 45(5): 79-84.
[7]	周迅;俞小莉. 曲轴疲劳裂纹扩展规律测试及形成机理分析[J]. , 2008, 44(1): 238-242.
[8]	浦瑞霆. 晶界时效析出物对Ni-Cr奥氏体钢高温低周疲劳裂纹萌生和扩展的影响[J]. , 1990, 26(1): 7-13.