海洋钻机起升系统绞车滚筒层间钢丝绳弯曲摩擦疲劳行为研究

doi:10.3901/JME.2025.12.104

摘要/Abstract

摘要： 海洋钻机起升系统绞车滚筒层间钢丝绳易发生弯曲摩擦疲劳行为，造成钢丝绳横截面积损耗和承载强度降低，进而制约起升系统钢丝绳承载安全性。因此，运用自制层间钢丝绳弯曲摩擦疲劳试验台，开展不同疲劳参数(疲劳次数、疲劳载荷和围包角)下钢丝绳弯曲摩擦疲劳试验，通过人工拆股法、超景深电子显微镜和扫描电子显微镜，考察了钢丝绳弯曲摩擦疲劳特性(摩擦因数、磨损轮廓尺寸、横截面损失面积、磨损机理、磨损体积及磨损速率)及其受到疲劳参数的影响规律。结果表明：疲劳钢丝绳摩擦因数呈现快速增加、缓慢增加及趋于稳定的变化趋势，随着疲劳载荷的增大而增大，随着围包角增大而减小；最大磨损宽度、磨损深度、磨损体积及横截面最大损失面积均随着疲劳次数和疲劳载荷增加而增加，随围包角增大而减小；磨损速率随着疲劳次数增加呈现快速增加-趋于稳定-小幅增长的变化趋势；磨损机理主要为氧化磨损、黏着磨损和疲劳磨损。

关键词: 钢丝绳, 弯曲, 摩擦疲劳, 疲劳载荷

Abstract: The bending tribo-fatigue behaviors of the wire rope between the layers of winch drums in the hoisting system of offshore rig is easy to occur, which results in the loss of the cross-sectional area and the reduction of the load-bearing strength of the rope, and then restricts the load-bearing safety of the ropes in the hoisting system. Therefore, the bending tribo-fatigue test of steel wire ropes under different fatigue parameters (fatigue cycles, fatigue load and wrap angle) is carried out by using a self-made test bench for bending tribo-fatigue of steel wire rope between layers. The bending tribo-fatigue characteristics (wear coefficient, wear profile, cross-sectional loss area, wear mechanisms, wear volume and wear rate) and the law of their influence by fatigue parameters are investigated. The results demonstrate that the friction coefficient of the fatigue wire rope exhibits a rapid initial increase, followed by a slower subsequent rise that ultimately stabilizes. It increases with higher fatigue load, while it decreases with an increase in wrapping angles. The maximum wear width, wear depth, wear volume, and the cross-sectional loss area all increase with fatigue cycles and fatigue loads, but decrease as the wrapping angle increases. The wear rate initially increases rapidly, stabilizes, and then shows a slight increase with the number of fatigue cycles. The primary wear mechanisms identified include oxidative wear, adhesive wear, and fatigue wear.

Key words: wire ropes, bending, tribo-fatigue, fatigue load

中图分类号:

TH117

种海浪, 王大刚, 张德坤. 海洋钻机起升系统绞车滚筒层间钢丝绳弯曲摩擦疲劳行为研究[J]. 机械工程学报, 2025, 61(12): 104-117.

CHONG Hailang, WANG Dagang, ZHANG Dekun. Study of Bending Tribo-fatigue Behaviors of Wire Rope between Layers of Winch Drum of Offshore Drilling Rig Hoisting System[J]. Journal of Mechanical Engineering, 2025, 61(12): 104-117.

导出引用管理器 EndNote|Reference Manager|ProCite|BibTeX|RefWorks

链接本文: http://www.cjmenet.com.cn/CN/10.3901/JME.2025.12.104

http://www.cjmenet.com.cn/CN/Y2025/V61/I12/104

参考文献

[1] LI C C，WANG D G，SUN Y W，et al. Bending fatigue damage behavior of wire rope in hoisting system of drilling rig[J]. Tribology International，2023，187：108745.
[2] 蔡运恒. 海洋钻机起升系统负荷特性研究[D]. 西安：西安工程大学，2016. CAI Yunheng. Research on the load characteristic of offshore drilling rig lifting system[D]. Xi’an：Xi’an Polytechnic University，2016.
[3] 孙跃威. 钻机起升钢丝绳弯曲疲劳试验系统研制及损伤行为研究[D]. 徐州：中国矿业大学，2023. SUN Yuewei. The development of bending fatigue testing system and damage behavior of hoisting rope of the drilling rig [D]. Xuzhou：China University of Mining and Technology，2023.
[4] STANOVA E，FEDORKO G，FABIAN M，et al. Computer modelling of wire strands and ropes Part I： Theory and computer implementation[J]. Advances in Engineering Software，2011，42(6)：305-315.
[5] WANG D G，ZHANG D K，GE S R. Finite element analysis of fretting fatigue behavior of steel wires and crack initiation characteristics[J]. Engineering Failure Analysis，2013，28：47-62.
[6] GUO Y B，ZHANG D K，YANG X H，et al. Experimental research on effect of wire rope transverse vibration on friction transmission stability in a friction hoisting system[J]. Tribology International，2017，115：233-245.
[7] ARGATOV I I，GÓMEZ X，TATO W，et al. Wear evolution in a stranded rope under cyclic bending： Implications to fatigue life estimation[J]. Wear，2011，271：2857-2867.
[8] OKSANEN V，VALTONEN K，ANDERSSON P，et al. Comparison of laboratory rolling–sliding wear tests with in-service wear of nodular cast iron rollers against wire ropes[J]. Wear，2015，340：73-81.
[9] MATEJIĆ M，BLAGOJEVIĆ M，MARJANOVIĆ V，et al. Tribological aspects of the process of winding the steel rope around the winch drum[J]. Tribology in Industry，2014，36(1)：90-96.
[10] XIANG L，WANG H Y，CHEN Y，et al. Modeling of multi-strand wire ropes subjected to axial tension and torsion loads[J]. International Journal of Solids and Structures，2015，58：233-246.
[11] 任志乾，于宗乐，陈循. 钢丝绳弹塑性损伤本构模型研究[J]. 机械工程学报，2017，53(1)：121-129. REN Zhiqian，YU Zongyue，CHEN Xun. Study on wire rope elastic-plastic damage constitutive model[J]. Journal of Mechanical Engineering，2017，53(1)：121-129.
[12] ZHANG J，WANG D G，SONG D Z，et al. Tribo-fatigue behaviors of steel wire rope under bending fatigue with the variable tension[J]. Wear，2019，428-429：154-161.
[13] 王大刚，张俊，朱辉龙，等. 定、变载弯曲疲劳钢丝绳失效机理对比研究[J]. 摩擦学学报，2020，40(6)：762-773. WANG Dagang，ZHANG Jun，ZHU Huilong，et al. Comparative research on failure mechanisms of steel wire ropes during bending fatigue under constant and variable loads[J]. Tribology，2020，40(6)：762-773.
[14] 殷觊恺，李济顺，邹声勇，等. D/d与绳端张力对钢丝绳弯曲应力和寿命的影响[J]. 煤矿安全，2017，48(1)：59-62. YIN Jikai，LI Jishun，ZOU Shengyong，et al. Influence of D/d and terminal tension on bending stress and service life of steel wire rope[J]. Safety in Coal Mines，2017，48(1)：59-62.
[15] HOBBS R E，GHAVANI K. The fatigue of structural wire strands[J]. International Journal of Fatigue，1982，4(2)：69-72.
[16] ARGATOV I I，Gómez X，Tato W，et al. Wear evolution in a stranded rope under cyclic bending：Implications to fatigue life estimation[J]. Wear，2011，271(11-12)：2857-2867.
[17] ZHANG D K，GENG H，ZHANG Z，et al. Investigation on the fretting fatigue behaviors of steel wires under different strain ratios[J]. Wear，2013，303(1-2)：334-342.
[18] ZHANG D K，YANG X，CHEN K，et al. Fretting fatigue behavior of steel wires contact interface under different crossing angles[J]. Wear，2018，400：52-61.
[19] 种海浪. 钢丝绳摩擦疲劳试验系统研制及界面摩擦学行为研究[D]. 徐州：中国矿业大学，2023. CHONG Hailang. Development of the tribo-fatigue testing system and research on interfacial tribological behaviors of the steel wire rope[D]. Xuzhou：China University of Mining and Technology，2023.
[20] FENG C N，ZHANG D K，GRECOV D，et al. Effect of rheological properties of friction-enhancing greases on the friction between friction lining and wire rope[J]. Tribology International，2020，144：106143.
[21] WANG B，WANG D G，TANG L，et al. Bending tribo-corrosion-fatigue behaviors between cable wire and saddle material in the suspension bridge[J]. Tribology International，2023，187：108711.
[22] 王博，王大刚，种海浪，等. 悬索桥主缆钢丝与鞍座材料摩擦腐蚀疲劳行为[J]. 机械工程学报，2023，59(21)：341-355. WANG Bo，WANG Danggang，CHONG Hailang，et al. Tribo-corrosion-fatigue behaviors of suspension bridge cable wires in contact with the saddle material[J]. Journal of Mechanical Engineering，2023，59(21)：341-355.
[23] 程志强，李春燕，高凯雄. 真空宽载下二硫化钼/碳复合薄膜的超低磨损机制[J]. 中国表面工程，2024，37(3)：175-184. CHENG Zhiqiang，LI Chunyan，GAO Kaixiong. Ultra-low wear mechanism of molybdenum disulfide/ carbon composite films under vacuum wide load[J]. China Surface Engineering，2024，37(3)：175-184.
[24] 魏晨阳，白琴，郭鹏，等. HiPIMS占空比对Al合金表面Ti/DLC涂层力学和摩擦性能的影响[J]. 中国表面工程，2023，36(4)：77-88. WEI Chenyang，BAI Qin，GUO Peng，et al. Effect of duty ratio on structure，mechanical and frictional properties of Ti/DLC coatings on Al alloy via HiPIMS[J]. China Surface Engineering，2023，36(4)：77-88.
[25] 李超，马国佳，孙刚，等. 基体偏压对316L不锈钢表面多层Ti-DLC薄膜摩擦及腐蚀行为的影响[J]. 中国表面工程，2023，36(1)：189-199. LI Chao，MA Guojia，SUN Gang，et al. Effects of substrate bias voltage on friction and corrosion behavior of multilayer Ti-DLC film on the surface of 316L stainless steel[J]. China Surface Engineering，2023，36(1)：189-199.
[26] 沈小满. 悬索桥主缆钢丝承载强度渐变劣化研究[D]. 徐州：中国矿业大学，2022. SHEN Xiaoman. Study on gradual deterioration of load-bearing strength of main cable steel wire of suspension bridge[D]. Xuzhou：China University of Mining and Technology，2022.
[27] 何东青，梁瑞瑞，冯子涵，等. 中间层厚度对Cr₃C₂-NiCr/DLC复合涂层腐蚀磨损行为的影响[J/OL]. 中国表面工程. https://link.cnki.net/urlid/11.3905.tg. 20241217.1919.029. HE Dongqing，LIANG Ruirui，FENG Zihan，et al. The influence of interlayer thicknesses on the tribo-corrosion behaviors of Cr₃C₂-NiCr/DLC duplex coatings[J/OL]. China Surface Engineering. https://link.cnki.net/ urlid/11.3905.tg.20241217.1919.029.
[28] WAND B，WANG D G，CHONG H L，et al. Tribo-corrosion interaction of the parallel steel wires in the suspension bridges[J]. Friction，2023，11：2221-2237.
[29] 管筱竹，郑贺，郭鹏，等. Si/O含量对DLC涂层腐蚀性能的影响[J]. 中国表面工程，2024，37(6)：283-296. GUAN Xiaozhu，ZHENG He，GUO Peng，et al. Effect of Si/O content on the long-term electrochemical corrosion performance of DLC coatings[J]. China Surface Engineering，2024，37(6)：283-296.
[30] 杜娟，高深远，虞文军，等. DLC薄膜对A100钢的摩擦学及力学性能影响[J/OL]. 中国表面工程. https://link.cnki.net/urlid/11.3905.tg.20241202.0922.002. DU Juan，GAO Shenyuan，YU Wenjun，et al. Influence of DLC film on the tribological and mechanical properties of A100 steel[J/OL]. China Surface Engineering. https://link.cnki.net/urlid/11.3905.tg. 20241202.0922.002.
[31] 周琼，岗志远，黄彪，等. 退火温度对DLC和Si-DLC涂层微观结构和摩擦学性能的影响[J]. 中国表面工程，2024，37(4)：206-217. ZHOU Qiong，GANG Zhiyuan，HUANG Biao，et al. Effect of annealing temperature on microstructure and tribological properties of DLC and Si-DLC coatings[J]. China Surface Engineering，2024，37(4)：206-217.
[32] 张绍筠，岳文，王艳艳，等. 清净剂、分散剂与ZDDP复配对a-C薄膜摩擦学性能的影响[J]. 中国表面工程，2023，36(6)：90-99. ZHANG Shaojun，YUE Wen，WANG Yanyan，et al. Effect of detergent，dispersant，and zinc dialkyldithiophosphate on the tribological properties of amorphous-C films[J]. China Surface Engineering，2023，36(6)：90-99.
[33] 李琪刚，陈仁德，李昊，等. 同步脉冲偏压对HiPIMS制备DLC薄膜结构和性能的影响[J/OL]. 中国表面工程. https://link.cnki.net/urlid/11.3905.TG.20241219. 1414. 002. LI Qigang，CHEN Rende，LI Hao，et al. Effect of synchronous pulsed-bias on structure and mechanical properties of DLC films by HiPIMS technique[J/OL]. China Surface Engineering. https://link.cnki.net/urlid/ 11.3905.TG.20241219.1414.002.
[34] 孙繁新，史彦斌，蒲吉斌，等. 苛刻空间环境下固体润滑涂层在谐波齿轮减速器表面的服役性能评价[J]. 中国表面工程，2023，36(5)：76-87. SHUN Fanxin，SHI Yanbin，PU Jibin，et al. Service performance evaluation of solid-lubrication coating on harmonic gear reducer surface in harsh space environment[J]. China Surface Engineering，2023，36(5)：76-87.