2219铝合金双轴肩搅拌摩擦焊工艺及接头组织性能研究

张海峰^1,2, 郝云飞³, 李高辉^1,2, 颜旭³, 杨海峰^1,2, 周利^1,2

1. 哈尔滨工业大学先进焊接与连接国家重点实验室哈尔滨 150001;
2. 哈尔滨工业大学(威海)山东省特种焊接技术重点实验室威海 264209;
3. 首都航天机械有限公司北京 100076

收稿日期:2021-12-11 修回日期:2022-04-20 出版日期:2022-11-20 发布日期:2023-02-07
通讯作者: 周利(通信作者),男,1982年出生,博士,副教授,博士研究生导师。主要研究方向为先进固相连接、焊接冶金与材料焊接性。E-mail:zhou.li@hit.edu.cn
作者简介:张海峰,男,1995年出生,硕士研究生。主要研究方向为轻质合金搅拌摩擦焊。E-mail:hfzhang_2019hit@163.com
基金资助:
十三五装备预研共用技术课题(41423050128);山东省重点研究开发(2018GGX103053)资助项目

Research on Welding Process and Joint Microstructure-properties of Bobbin Tool Friction Stir Weld for 2219 Aluminum Alloy

ZHANG Hai-feng^1,2, HAO Yun-fei³, LI Gao-hui^1,2, YAN Xu³, YANG Hai-feng^1,2, ZHOU Li^1,2

1. State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001;
2. Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209;
3. Capital Aerospace Machinery Corporation, Beijing 100076

Received:2021-12-11 Revised:2022-04-20 Online:2022-11-20 Published:2023-02-07

摘要/Abstract

摘要： 通过对8mm厚2219铝合金进行双轴肩搅拌摩擦焊试验,研究了不同焊接速度对接头成形、组织演变及其对力学性能的影响规律。工艺试验结果表明:在固定转速(200r/min)下,不同焊接速度下的接头均成形良好,未出现微裂纹、隧道以及疏松等焊缝表面缺陷。随着焊接速度的增加,接头区域晶粒尺寸减小;接头显微硬度受到晶粒尺寸与沉淀相分布的制约,硬度分布曲线呈“W”形,热影响区硬度最低。并且随着焊接速度的增加,接头最低硬度和抗拉强度逐渐提高,断裂位置发生在热影响区与热影响区交界处。在焊接速度为350mm/min时,接头抗拉强度达到最大值335MPa,约为母材的72.8%。

关键词: 双轴肩搅拌摩擦焊, 2219铝合金, 组织与性能

Abstract: Bobbin tool friction stir welding of 8 mm thick 2219 aluminum alloy sheets is carried out, and the influence of welding speed on the microstructure and mechanical properties of the welded joints are investigated. The results show that at the rotational rate is 200 r/min, sound joints can be obtained under the various welding speeds. As the welding speed increases, the heat input decreases,so that the size of the recrystallized grains gradually decreases. The hardness change of 2219 aluminum alloy can be attributed to the distribution of precipitates phase particles and the heterogeneity of grains. The lowest hardness zones are located at the heat-affected zones of the joint. With the increase of welding speed, the lowest hardness and tensile strength of the welded joints increase gradually.The welded joints fracture in the boundary of the HAZ and TMAZ. When the welding speed is 350 mm/min, the tensile strength reaches the maximum value of 335 MPa, which corresponds to 72.8% of that of the base metal.

Key words: bobbin tool friction stir welding, 2219 aluminum alloy, microstructure and mechanical properties

中图分类号:

TG457

张海峰, 郝云飞, 李高辉, 颜旭, 杨海峰, 周利. 2219铝合金双轴肩搅拌摩擦焊工艺及接头组织性能研究[J]. 机械工程学报, 2022, 58(22): 250-257.

ZHANG Hai-feng, HAO Yun-fei, LI Gao-hui, YAN Xu, YANG Hai-feng, ZHOU Li. Research on Welding Process and Joint Microstructure-properties of Bobbin Tool Friction Stir Weld for 2219 Aluminum Alloy[J]. Journal of Mechanical Engineering, 2022, 58(22): 250-257.

参考文献

[1] 何海林. 2219铝合金大型环件组织性能调控方法与工程应用研究[D].长沙:中南大学,2019.HE Hailin. Microstructure and properties of 2219aluminum alloy large ring and its engineering application[D].Changsha:Central South University,2019.
[2] ANDREAS B, THOMAS G, CHRISTOPH P, et al.Characterization of the microstructure in friction stir welds of EN AW-2219 using coincident Doppler-broadening spectroscopy[J].Materials Characterization,2019,149(1):143-152.
[3] 康举,李吉超,冯志操,等. 2219-T8铝合金搅拌摩擦焊接头力学和应力腐蚀性能薄弱区研究[J].金属学报,2016,52(1):60-70.KANG Ju,LI Jizhao,FANG Zhichao,et al. Investigation on mechanical and stress corrosion cracking properties of weakness zone in friction stir welded 2219-T8 Al alloy[J].Acta Metallurgica Sinica,2016,52(1):60-70.
[4] HU Y Y,LIU H J,FUJII H. Improving the mechanical properties of 2219-T6 aluminum alloy joints by ultrasonic vibrations during friction stir welding[J]. Journal of Materials Processing Tech.,2019,271(1):75-84.
[5] MISHRA R S, MA Z Y. Friction stir welding and processing[J]. Materials Science and Engineering R,2005,50(1):1-78.
[6] VIVEK P, LI W Y, ACHILLES V, et al. Recent development in friction stir processing as a solid-state grain refinement technique:Microstructural evolution and property enhancement[J]. Critical Reviews in Solid State and Materials Sciences,2019,44(5):378-426.
[7] XUE P,ZHANG X X,WU L H,et al. Research process on friction stir welding and processing[J]. Acta Metallurgica Sinica,2016,52(10):1222-1238.
[8] CAM G. Friction stir welded structural materials:Beyond Al-alloys[J]. International Materials Reviews, 2011,56(1):1-48.
[9] GUO Q H,DONG X C,HAO M W,et al. Effect of tool probe with a disc at the top on the microstructure and mechanical properties of FSW joints for 6061-T6 aluminum alloy[J]. Journal of Adhesion Science and Technology,2019,33(22):2462-2475.
[10] THOMAS W M,WIESNER C S. Recent developments of FSW technologies:Evaluation of root defects,composite refractory tools for steel joining and one-pass welding of thick sections using self-reacting bobbin tools[C]//8th International Conference on Trends in Welding Research,Pine Mountain,United States. 2008.
[11] 乔亚霞,彭杏娜,张鹏飞,等.国内搅拌摩擦焊技术在输变电领域的应用现状及发展前景[J].焊接,2019(4):34-38,66-67.QIAO Yaqia,PENG Xinna,ZHANG Pengfei,et al.Application and development prospect of friction stir welding technology in power transmission and transformation field in China[J]. Welding&Joining,2019(4):34-38,66-67.
[12] 杨亚楠,刘振邦,仪家良.搅拌摩擦焊技术应用现状与发展趋势[J].工程技术研究,2017(2):57-58.YANG Yanan,LIU Zhenbang,YI Jialiang. Application status and development trend of friction stir welding technology[J]. Engineering Technology and Application,2017(2):57-58.
[13] SKINNER M,EDWARDS R L. Improvements to the FSW process using the self-reacting technology[C]//Materials Science Forum. 2003,426:2849-2854.
[14] 刘朝磊. 6061铝合金双轴肩搅拌摩擦焊工艺及机理研究[D].哈尔滨:哈尔滨工业大学,2015.LIU Chaolei. Research on process and mechanism of selr-reacting friction stir welding for 6061 aluminum alloy[D]. Harbin:Harbin Institute of Technology,2015.
[15] WAN L,HUANG Y X,LV Z L,et al. Effect of self-support friction stir welding on microstructure and microhardness of 6082-T6 aluminum alloy joint[J].Materials and Design,2014,55:197-203.
[16] 张健,李光,李从卿,等. 2219-T4铝合金双轴肩FSW与常规FSW接头性能对比研究[J].焊接,2008(11):50-52.ZHANG Jian,LI Guang,LI Congqing,et al. Comparison of joint properties of AA2219-T4 between conventional FSW and bobbin-tool FSW[J]. Welding&Joining,2008(11):50-52.
[17] ZHANG H T,SONG J Q. Microstructural evolution of aluminum magnesium lap joints welded using MIG process with zinc foil as an interlayer[J]. Materials Letters,2011,65(21-22):3292-3299.
[18] XU W F,LUO Y X,ZHANG W,et al. Comparative study on local and global mechanical properties of bobbin tool and conventional friction stir welded 7085-T7452aluminum thick plate[J]. Journal of Materials Science&Technology,2018,34(1):173-184.
[19] FENG X L,LIU H J,LIPPOLD J C. Microstructure characterization of the stir zone of submerged friction stir processed aluminum alloy 2219[J]. Materials Characterization,2013,82:97-102.
[20] XU W,LIU J,LUAN G,et al. Microstructure and mechanical properties of friction stir welded joints in 2219-T6 aluminum alloy[J]. Mater. Des.,2009,30:3460-3467.
[21] LIU H,ZHANG H,YU L. Effect of welding speed on microstructures and mechanical properties of underwater friction stir welded 2219 aluminum alloy[J]. Material Design,2011,32:1548-1553.
[22] 汤智茂,湛利华,徐永谦,等.时效热处理对2219铝合金搅拌摩擦焊焊缝组织性能的影响[J].塑性工程学报,2021,28(5):134-144.TANG Zhimao,ZHAN Lihua,XU Yongqian,et al. Effect of aging heat treatment on microstructure and properties of friction stir welding seam of 2219 aluminum alloy[J].Journal of Plasticity Engineering,2021,28(5):134-144.
[23] LI J Q, LIU H J. Effects of welding speed on microstructures and mechanical properties of AA2219-T6welded by the reverse dual-rotation friction stir welding[J].The International Journal of Advanced Manufacturing Technology,2013,68(9-12):2071-2083.

2219铝合金双轴肩搅拌摩擦焊工艺及接头组织性能研究

Research on Welding Process and Joint Microstructure-properties of Bobbin Tool Friction Stir Weld for 2219 Aluminum Alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐

Metrics

本文评价

[1]	林智雄, 邵震, 梁鑫裕, 崔雷, 王东坡, 谢燕, 黄一鸣, 杨立军. 2219铝合金拉拔式摩擦塞补焊成形过程分析[J]. 机械工程学报, 2024, 60(20): 144-152.
[2]	毛献昌, 易幼平, 黄始全, 何海林. 多向锻造变形温度对2219铝合金微观组织和力学性能的影响[J]. 机械工程学报, 2023, 59(22): 275-286.
[3]	安剑, 李永丰, 张云光, 李淑慧. 热冲压条件下2219铝合金的本构行为测试与建模[J]. 机械工程学报, 2021, 57(4): 44-52.
[4]	高炼玲, 余圣甫, 禹润缜, 何天英, 史玉升. 5356铝合金过渡端框电弧增材制造及组织与性能[J]. 机械工程学报, 2020, 56(8): 28-36.
[5]	邹阳帆, 王非凡, 李文亚, 禇强, 汤化伟, 崔凡. 不等厚2219铝合金板回填式搅拌摩擦点焊接头组织及性能研究[J]. 机械工程学报, 2020, 56(6): 176-183.
[6]	赵俊杰, 宿浩, 石磊, 武传松. 超声功率对UVeFSW铝-镁合金异质接头组织与性能的影响[J]. 机械工程学报, 2020, 56(6): 24-32.
[7]	饶项炜, 顾冬冬, 席丽霞. 选区激光熔化成形碳纳米管增强铝基复合材料成形机制及力学性能研究[J]. 机械工程学报, 2019, 55(15): 1-9.
[8]	刘杰, 陈向阳, 范彦斌. 选区激光熔化成形H13钢缺陷、组织调控及拉伸性能[J]. 机械工程学报, 2018, 54(16): 101-107.
[9]	张乐福, 马武江, 何龙, 张浩, 王元华, 邓松, 刘庆冬. 小型反应堆用A508-3钢管板锻件(国产)的显微组织和力学性能均匀性研究[J]. 机械工程学报, 2018, 54(10): 103-109.
[10]	鲁世强;李鑫;王克鲁;董显娟;李臻熙;曹春晓. 用于控制材料热加工组织与性能的动态材料模型理论及其应用[J]. , 2007, 43(8): 77-85.