NiTi气雾化制粉工艺对选区激光熔化成型性、制件超弹性的影响

doi:10.3901/JME.2020.15.104

机械工程学报 ›› 2020, Vol. 56 ›› Issue (15): 104-109.doi: 10.3901/JME.2020.15.104

• 特邀专栏：4D打印技术 • 上一篇下一篇

扫码分享

NiTi气雾化制粉工艺对选区激光熔化成型性、制件超弹性的影响

郑聃¹, 李瑞迪¹, 宋波², 熊熠¹, 袁铁锤¹, 史玉升²

1. 中南大学粉末冶金国家重点实验室长沙 410083;
2. 华中科技大学材料成形与模具技术国家重点实验室武汉 430074

收稿日期:2019-09-19 修回日期:2019-11-28 出版日期:2020-08-05 发布日期:2020-10-19
通讯作者: 李瑞迪(通信作者),男,1983年出生,博士,副教授,博士研究生导师。主要研究方向为3D打印粉末设计、制备与应用。E-mail:liruidi@126.com
作者简介:郑聃,男,1993年出生。主要研究方向为4D打印形状记忆合金。E-mail:csuzhd@csu.edu.cn
基金资助:
中南大学自由探索创新资助项目（502211909）。

Effect of NiTi Powder Gas Atomization Process on the Selective Laser Melting Moldability and Alloys' Superelastic

ZHENG Dan¹, LI Ruidi¹, SONG Bo², XIONG Yi¹, YUAN Tiechui¹, SHI Yusheng²

1. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083;
2. State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074

Received:2019-09-19 Revised:2019-11-28 Online:2020-08-05 Published:2020-10-19

摘要/Abstract

摘要： 选区激光熔化成型具有外界温度感知能力的NiTi形状记忆合金是4D打印金属材料技术的基础研究，根据选区激光熔化技术对粉末性能的要求，研究NiTi形状记忆合金不同气雾化制粉工艺对选区激光熔化成型性及制件超弹性的影响规律具有重要意义。通过对比分析真空惰性气体雾化（VIGA）、电极感应熔炼气雾化（EIGA）制粉工艺对NiTi合金粉末杂质含量、流动性、球形度等性能的影响，发现VIGA制粉工艺由于采用坩埚熔炼，导致合金杂质元素增加、粉体性能恶化，粉末粒度分布偏向细粉侧，极易形成卫星粉，导致粉末流动性差，在打印过程中铺粉困难而难以成型，并且氧含量的增加导致打印过程中易发生球化、开裂等现象，使得VIGA工艺制备的NiTi合金粉末SLM成型性较差。而采用EIGA工艺制备的粉末粒度分布均匀、流动性好、氧含量低，满足选区激光熔化技术对NiTi合金粉末的特性要求。并对比分析两种工艺制备的粉末打印样品的表面形貌，成型了具有完全回复性能的超弹NiTi形状记忆合金样件。

关键词: 选区激光熔化, NiTi形状记忆合金粉末, 真空熔炼气雾化, 电极感应熔炼气雾化

Abstract: Selective laser melting NiTi shape memory alloy which has ambient temperature sensing capability is the basic of a metal material 4D printing technology, according to the technical requirements for selective laser melting the powder properties, studying the effect of NiTi powder gas atomization process on the selective laser melting moldability and alloys’ superelastic is great significant. By comparing the influence of vacuum inert gas atomization (VIGA) and electrode induction melting gas atomization (EIGA) process on the performance of NiTi alloy powder, such as the impurity content, fluidity, spherical degree. The VIGA process which used crucible melting resulting in impurity content is higher than EIGA process, and fine powder size distribution biased side, easy to form satellite powder, resulting in poor powder flow, and powder spreading difficulties in the printing process and difficult to mold, more than of that, increasing the oxygen content results in balling in the SLM process, prone to cracking and so on, hence the NiTi alloy powder prepared by VIGA process is poor moldability in SLM process. EIGA prepared NiTi powder hold homogeneous particle size distribution, good fluidity and low oxygen content, satisfying selective laser melting technique NiTi alloy powder characteristics requirements. Comparison of surface topography and powder samples prepared from two printing processes, forming a superelastic NiTi shape memory alloy sample having a complete ecovery properties.

Key words: selective laser melting, NiTi shape mempry alloy powder, VIGA, EIGA

中图分类号:

TF123

郑聃, 李瑞迪, 宋波, 熊熠, 袁铁锤, 史玉升. NiTi气雾化制粉工艺对选区激光熔化成型性、制件超弹性的影响[J]. 机械工程学报, 2020, 56(15): 104-109.

ZHENG Dan, LI Ruidi, SONG Bo, XIONG Yi, YUAN Tiechui, SHI Yusheng. Effect of NiTi Powder Gas Atomization Process on the Selective Laser Melting Moldability and Alloys' Superelastic[J]. Journal of Mechanical Engineering, 2020, 56(15): 104-109.

参考文献

[1] TIBBITS S. The emergence of "4D printing"[C/OL].[2013-02]. http:ted.com/talks/skylar_tibbits_the_emergence_of_4d_printing.
[2] RASTOGI P,KANDASUBRAMANIAN B. Breakthrough in the printing tactics for stimuli-responsive materials:4D printing[J]. Chemical Engineering Journal,2019,366:264-304.
[3] MOMENI F,SEYED M H N S,LIU X,et al. A review of 4D printing[J]. Materials & Design,2017,122:42-79.
[4] GLADMAN A S,MATSUMOTO E A,NUZZO R G,et al. Biomimetic 4D printing[J]. Nature Materals,2016,15:413-418.
[5] ZAREK M,LAYANI M,COOPERSTEIN I,et al. 3D printing of shape memory polymers for flexible electronic devices[J]. Advanced Materials,2016,28(22):4449-4454.
[6] KIRILLOVA A,MAXSON R,STOYCHEV G,et al. 4D biofabrication using shape-morphing hydrogels[J]. Advanced Materials,2017,29(46):1703443.
[7] YANG H,LEOW W R,WANG T,et al. 3D Printed photoresponsive devices based on shape memory composites[J]. Advanced Materials,2017,29(33):1701627.
[8] TRUBY R L,LEWIS J A. Printing soft matter in three dimensions[J]. Nature,2016,540(7633):371-378.
[9] CHEN X,LIU X,OUYANG M,et al. Multi-metal 4D printing with a desktop electrochemical 3D printer[J]. Scientific Reports,2019,9(1):1917-1928.
[10] SAEDI S,SHAYESTEH M N,AMERINATANZI A,et al. On the effects of selective laser melting process parameters on microstructure and thermomechanical response of Ni-rich NiTi[J]. Acta Materialia,2018,144:552-560.
[11] GU D,HE B. Finite element simulation and experimental investigation of residual stresses in selective laser melted Ti-Ni shape memory alloy[J]. Computational Materials Science,2016,117:221-232.
[12] YANG Y,ZHAN J B,LI B,et al. Laser beam energy dependence of martensitic transformation in SLM fabricated NiTi shape memory alloy[J]. Materialia,2019,6:100305.
[13] 杨启云,吴文恒,张亮,等. EIGA雾化法制备3D打印用Ti6Al4V合金粉末[J]. 粉末冶金工业,2018,28(3):8-12. YANG Qiyun,WU Wenheng,ZHANG Liang,et al. Ti6Al4V alloy powder prepared by electro de induction-melting inert gas atomization for 3D printing[J]. Powder Metallurgy Industry,2018,28(3):8-12.
[14] 戴永年,杨斌. 有色金属材料的真空熔炼[M]. 北京:机械工业出版社,2000. DAI Yongnian,YANG Bin. Vacuum melting of nonferrous metal materials[M]. Beijing:China Machine Press,2000.
[15] 黄培云. 粉末冶金原理[M]. 北京:冶金工业出版社,1997. HUANG Peiyun. Principles of powder metallurgy[M]. Beijing:Metallurgical Industry Press,1997.
[16] 魏明炜,陈岁元,郭快快,等. EIGA制备激光3D打印用TA15钛合金粉末[J]. 材料导报,2017,31(6):64-78 WEI Mingwei,CHEN Suiyuan,GUO Kuaikuai,et al. Preparation of TA15 Titannium alloy powder by EIGA for laser 3D printing[J]. Material Review,2017,31(6):64-78.
[17] LI R,LIU J,SHI Y,et al. Balling behavior of stainless steel and nickel powder during selective laser melting process[J]. The International Journal of Advanced Manufacturing Technology. 2012,59(9-12):1025-1035.
[18] 舟久保,熙康. 形状记忆合金[M]. 北京:机械工业出版社,1992. ZHOU Jiubao,XI Kang. Shape memory alloy[M]. Beijing:China Machine Press,1992.

NiTi气雾化制粉工艺对选区激光熔化成型性、制件超弹性的影响

Effect of NiTi Powder Gas Atomization Process on the Selective Laser Melting Moldability and Alloys' Superelastic

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐

Metrics

本文评价

[1]	石岩, 张恒. 面向选区激光熔化增材制造的多孔结构设计与力学性能分析[J]. 机械工程学报, 2023, 59(18): 175-185.
[2]	黄祥辉, 曹睿博, 郑睿恒, 马飞豪, 蒋益雪, 詹章瑜, 于天宇, 康楠. 选区激光熔化NiTi形状记忆合金成形与热处理[J]. 机械工程学报, 2023, 59(17): 250-257.
[3]	林开杰, 董伟菘, 顾冬冬, 全景峰, 乔竞驰, 王超超. 选区激光熔化工艺参数对燃料电池316L不锈钢双极板性能的影响[J]. 机械工程学报, 2021, 57(9): 167-174.
[4]	李永欣, 郭长春, 李凯伦, 于天. SLM制备的小长径比四棱锥点阵填充轻量化研究[J]. 机械工程学报, 2021, 57(24): 132-138.
[5]	张超, 周雷, 赵聪, 汪帅, 赫泰然, 祝毅, 杨华勇. 轻量节能型液压阀块设计与增材制造[J]. 机械工程学报, 2021, 57(24): 123-131.
[6]	李祺祺, 温耀杰, 张百成, 曲选辉. 梯度功能合金的增材制造技术研究进展[J]. 机械工程学报, 2021, 57(22): 184-200.
[7]	王硕, 丰焱, 林鑫. 选区激光熔化成型Ni50.8Ti49.2形状记忆合金的组织和性能研究[J]. 机械工程学报, 2020, 56(15): 46-52.
[8]	饶项炜, 顾冬冬, 席丽霞. 选区激光熔化成形碳纳米管增强铝基复合材料成形机制及力学性能研究[J]. 机械工程学报, 2019, 55(15): 1-9.
[9]	刘杰, 陈向阳, 范彦斌. 选区激光熔化成形H13钢缺陷、组织调控及拉伸性能[J]. 机械工程学报, 2018, 54(16): 101-107.
[10]	吴伟辉;杨永强. 选区激光熔化快速成形系统的关键技术[J]. , 2007, 43(8): 175-180.