能量密度对激光选区熔化成形AlSi10Mg合金缺陷及力学性能的影响

doi:10.3901/JME.2020.24.096

机械工程学报 ›› 2020, Vol. 56 ›› Issue (24): 96-105.doi: 10.3901/JME.2020.24.096

扫码分享

能量密度对激光选区熔化成形AlSi10Mg合金缺陷及力学性能的影响

闫泰起¹, 唐鹏钧¹, 陈冰清¹, 高祥熙¹, 楚瑞坤², 熊华平¹

1. 中国航发北京航空材料研究院3D打印研究与工程技术中心北京 100095;
2. 飞而康快速制造科技有限责任公司无锡 214145

收稿日期:2020-06-09 修回日期:2020-09-02 出版日期:2020-12-20 发布日期:2021-02-05
通讯作者: 陈冰清(通信作者),女,1984年出生,博士,研究员。主要研究方向为航空金属材料增材制造。E-mail:hwtkjcbq1984@163.com
作者简介:闫泰起,男,1993年出生。主要研究方向为航空金属材料增材制造。E-mail:18201165269@163.com

Effect of Energy Density on Defects and Mechanical Properties of AlSi10Mg Alloy Fabricated by Selective Laser Melting

YAN Taiqi¹, TANG Pengjun¹, CHEN Bingqing¹, GAO Xiangxi¹, CHU Ruikun², XIONG Huaping¹

1. 3D Printing Research and Engineering Technology Center, AECC Beijing Institute of Aeronautical Materials, Beijing 100095;
2. Falcon Fast Manufacturing Technology Co., Ltd., Wuxi 214145

Received:2020-06-09 Revised:2020-09-02 Online:2020-12-20 Published:2021-02-05

摘要/Abstract

摘要： 分析了能量密度对激光选区熔化成形AlSi10Mg合金致密度的影响规律，并采用微纳CT检测结合EDS能谱分析的方法，统计了试样内部缺陷的类型和尺寸，分析了缺陷在试样三维层面上的分布规律及产生原因，得出了影响激光选区熔化成形AlSi10Mg合金致密度和内部缺陷的主要因素。结果表明，合适的激光能量输入是获得高致密度的关键，当激光能量密度处于47.62~50.00 J/mm³区间时，试样致密度最高，此时试样中夹杂缺陷消失，孔洞缺陷最大尺寸降至0.056 mm。孔洞缺陷产生原因主要与未熔粉体、空心粉及氧化物有关。在优选激光能量密度区间内成形的AlSi10Mg合金试样，其平均抗拉强度和伸长率分别在294 MPa和8.0%以上，优于铸造AlSi10Mg合金。

关键词: 激光选区熔化成形, AlSi10Mg, 致密度, 孔洞缺陷, 拉伸性能

Abstract: The influence of energy density on relative density of the formed AlSi10Mg alloy is analyzed, and the types as well as sizes of internal defects in AlSi10Mg samples are counted by micro-nano CT detection together with energy dispersive spectrometer (EDS) analysis. The three-dimensional distribution and causes of defects with the samples are analyzed, and the main factors affecting the relative density as well as internal defects of selective laser melting fabricated AlSi10Mg alloy are put forward. It is shown that appropriate laser energy input is the key to obtain high density. When the laser energy density is in the range of 47.62-50.00 J/mm³, the samples have the highest density, the inclusion defects disappear and the maximum size of the hole defects reduce to 0.056 mm. The causes of hole defects are mainly related to unmelted powder, hollow powder and oxides. The average tensile strength and elongation of AlSi10Mg alloy fabricated under the optimum laser energy density range are above 294 MPa and 8.0%, respectively, which are higher than those of cast AlSi10Mg alloy.

Key words: selective laser melting, AlSi10Mg, relative density, hole defects, tensile properties

中图分类号:

TN249

闫泰起, 唐鹏钧, 陈冰清, 高祥熙, 楚瑞坤, 熊华平. 能量密度对激光选区熔化成形AlSi10Mg合金缺陷及力学性能的影响[J]. 机械工程学报, 2020, 56(24): 96-105.

YAN Taiqi, TANG Pengjun, CHEN Bingqing, GAO Xiangxi, CHU Ruikun, XIONG Huaping. Effect of Energy Density on Defects and Mechanical Properties of AlSi10Mg Alloy Fabricated by Selective Laser Melting[J]. Journal of Mechanical Engineering, 2020, 56(24): 96-105.

参考文献

[1] READ N,WANG W,ESSA K,et al. Selective laser melting of AlSi10Mg alloy:Process optimization and mechanical properties development[J]. Materials & Design,2015,65:417-424.
[2] HEINZ A,HASZLER A,KEIDEL C,et al. Recent development in aluminium alloys for aerospace applications[J]. Materials Science & Engineering A,2000,280(1):102-107.
[3] YADROITSEV I,SMUROV I. Selective laser melting technology:From the single laser melted track stability to 3D parts of complex shape[J]. Physics Procedia,2010,5(part-PB):551-560.
[4] 刘伟,李能,周标,等. 复杂结构与高性能材料增材制造技术进展[J]. 机械工程学报,2019,55(20):128-143. LIU Wei,LI Neng,ZHOU Biao,et al. Progress in additive manufacturing on complex structures and high-performance materials[J]. Journal of Mechanical Engineering,2019,55(20):128-143.
[5] OLAKANMI E O,COCHRANE R F,DALGARNO K W. A review on selective laser sintering/melting (SLS/SLM) of aluminium alloy powders:Processing,microstructure,and properties[J]. Progress in Materials Science,2015,74:401-477.
[6] 杨强,鲁中良,黄福享,等. 激光增材制造技术的研究现状及发展趋势[J]. 航空制造技术,2016,507(12):26-31. YANG Qiang,LU Zhongliang,HUANG Fuxiang,et al. Research on status and development trend of laser additive manufacturing[J]. Aeronautical Manufacturing Technology,2016,507(12):26-31.
[7] 李瑞迪,魏青松,刘锦辉,等. 选择性激光熔化成形关键基础问题的研究进展[J]. 航空制造技术,2012,401(5):26-31. LI Ruidi,WEI Qingsong,LIU Jinhui,et al. Research progress of key basic issue in selective laser melting of metallic powder[J]. Aeronautical Manufacturing Technology,2012,401(5):26-31.
[8] 孙成伟,陆启生,范正修,等. 激光辐射效应[M]. 北京:国防工业出版社,2002. SUN Chengwei,LU Qisheng,FAN Zhengxiu,et al. Laser radiation effect[M]. Beijing:National Defence Industrial Press,2002.
[9] 王霄,王东生,高雪松,等. 轻合金构件激光增材制造研究现状及其发展[J]. 应用激光,2016,36(4):478-483. WANG Xiao,WANG Dongsheng,GAO Xuesong,et al. Research status and development in laser additive manufacturing of light alloy components[J]. Applied Laser,2016,36(4):478-483.
[10] 董鹏,李忠华,严振宇,等. 铝合金激光选区熔化成形技术研究现状[J]. 应用激光,2015,35(5):607-611. DONG Peng,LI Zhonghua,YAN Zhenyu,et al. Research status of selective laser melting of aluminum alloys[J]. Applied Laser,2015,35(5):607-611.
[11] ABOULKHAIR N T,EVERITT N M,ASHCROFT I,et al. Reducing porosity in AlSi10Mg parts processed by selective laser melting[J]. Additive Manufacturing,2014(1):77-86.
[12] KEMPEN K,THIJS L,HUMBEECK J V,et al. Processing AlSi10Mg by selective laser melting:Parameter optimization and material characterization[J]. Materials Science and Technology,2015,31(8):917-923.
[13] WEI P,WEI Z,CHEN Z,et al. The AlSi10Mg samples produced by selective laser melting:single track,densification,microstructure and mechanical behavior[J]. Applied Surface Science,2017,408:38-50.
[14] 张文奇,朱海红,胡志恒,等. AlSi10Mg的激光选区熔化成形研究[J]. 金属学报,2017(8):24-32. ZHANG Wenqi,ZHU Haihong,HU Zhiheng,et al. Study on the selective laser melting of AlSi10Mg[J]. Acta Metallurgica Sinica,2017(8):24-32.
[15] XU Z,ZHANG J,ZHENG H,et al. Morphology and mechanical properties of PS/Al₂O₃ nanocomposites based on selective laser sintering[J]. Journal of Materials Science and Technology. 2005,21(6):866-870.
[16] SIMCHI A. Direct laser sintering of metal powders:Mechanism,kinetics and microstructural features[J]. Material Science and Engineering A. 2006,428(1-2):148-158.
[17] JUE J,GU D,CHANG K. Microstructure evolution and mechanical properties of Al-Al₂O₃ composites fabricated by selective laser melting[J]. Powder Technology,2017,310:80-91.
[18] LI N,HUANG S,ZHANG G D,et al. Progress in additive manufacturing on new materials[J]. Journal of Materials Science & Technology,2019(2):242-269.
[19] 杨启云,许炯恺,吴凯琦,等. 选区激光熔化成形用GH4169合金粉末的性能[J]. 粉末冶金工业,2020,30(3):9-13. YANG Qiyun,XU Jiongkai,WU Kaiqi,et al. Characteristic of GH4169 alloy powder used in selective laser melting[J]. Powder Metallurgy Industry,2020,30(3):9-13.
[20] 李能,熊华平,秦仁耀,等. 原位反应制备Ti₂AlNb/TiC+Ti₃SiC₂梯度材料的激光熔覆组织及成形机理[J]. 机械工程学报,2018(8):144-150. LI Neng,XIONG Huaping,QIN Renyao,et al. Microstructure and mechanism of Ti₂AlNb/TiC+Ti₃SiC₂ gradient materials by in-situ reaction laser cladding[J]. Journal of Mechanical Engineering,2018(8):144-150.
[21] 闫泰起,唐鹏钧,陈冰清,等. 退火温度对激光选区熔化AlSi10Mg合金微观组织及拉伸性能的影响[J]. 机械工程学报,2020,56(8):37-45. YAN Taiqi,TANG Pengjun,CHEN Bingqing,et al. Effect of annealing temperature on microstructure and tensile properties of AlSi10Mg alloy fabricated by selective laser melting[J]. Journal of Mechanical Engineering,2020,56(8):37-45.
[22] 黄伯云,李成功,石力开,等. 中国材料工程大典[M]. 北京:化学工业出版社,2005. HUANG Boyun,LI Chenggong,SHI Likai,et al. China materials engineering canon[M]. Beijing:Chemical Industry Press,2005.
[23] 张伟. 共晶Al-Si合金的硅相形貌控制及其对合金断裂韧性、疲劳裂纹扩展行为的影响[D]. 郑州:郑州大学,2007. ZHANG Wei. Control of Si morphology in eutectic Al-Si alloy and its effect on fracture toughness and fatigue growth of the alloy[D]. Zhengzhou:Zhengzhou University,2007.

能量密度对激光选区熔化成形AlSi10Mg合金缺陷及力学性能的影响

Effect of Energy Density on Defects and Mechanical Properties of AlSi10Mg Alloy Fabricated by Selective Laser Melting

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 14

编辑推荐

Metrics

本文评价

[1]	徐刚, 罗开玉, 鲁金忠. 激光定向能量沉积IN718/316L异质金属结构界面组织及力学性能研究[J]. 机械工程学报, 2024, 60(1): 179-189.
[2]	谢寅, 滕庆, 孙闪闪, 程坦, 白洁, 马瑞, 蔡超, 魏青松. 热等静压温度对激光选区熔化成形GH3536裂纹和组织性能的影响[J]. 机械工程学报, 2023, 59(4): 25-33.
[3]	赵庚, 方金祥, 张显程. 基于微米压入的延性金属单轴拉伸性能与断裂韧性评价技术研究进展[J]. 机械工程学报, 2023, 59(2): 51-68.
[4]	黄祥辉, 曹睿博, 郑睿恒, 马飞豪, 蒋益雪, 詹章瑜, 于天宇, 康楠. 选区激光熔化NiTi形状记忆合金成形与热处理[J]. 机械工程学报, 2023, 59(17): 250-257.
[5]	李鑫桐, 王帅, 杜佳鑫, 缪宇新, 陆皓, 徐济进. GO/AlSi10Mg激光熔化沉积组织性能研究[J]. 机械工程学报, 2023, 59(1): 309-318.
[6]	王磊磊, 吕飞阅, 高转妮, 虞文军, 高川云, 占小红. 电弧增材制造2319铝合金交叉桁条结构微观组织与拉伸性能研究[J]. 机械工程学报, 2023, 59(1): 267-277.
[7]	白玉超, 陈杰, 刘林青, 韦雄棉, 王迪. 热处理对增材制造AlSi10Mg超精密车削特性的影响机理[J]. 机械工程学报, 2022, 58(19): 315-330.
[8]	吴润宝, 徐刚, 罗开玉, 王长雨, 鲁金忠. 热处理对激光增材In718/316L功能梯度材料组织和性能的影响[J]. 机械工程学报, 2022, 58(19): 293-305.
[9]	闫泰起, 唐鹏钧, 陈冰清, 楚瑞坤, 郭绍庆, 熊华平. 退火温度对激光选区熔化AlSi10Mg合金微观组织及拉伸性能的影响[J]. 机械工程学报, 2020, 56(8): 37-45.
[10]	曹旭祥, 颜廷俊, 李鹏鹏, 王亭沂, 李风. 热采井口装置材料30CrMo的拉伸及蠕变性能研究[J]. 机械工程学报, 2020, 56(22): 112-119.
[11]	赵玉华, 满佳乐, 刘玉林, 陆皖皖. 凝固速度及热处理工艺对Al-8Ca组织性能的影响[J]. 机械工程学报, 2018, 54(18): 62-67.
[12]	赵德望, 任大鑫, 赵坤民, 郭杏林, 杨文平. 工艺参数对镁钛异质金属超声波点焊接头拉伸性能及疲劳性能的影响[J]. 机械工程学报, 2017, 53(24): 118-125.
[13]	刘会杰, 刘向前, 胡琰莹. 搅拌摩擦焊缝类型对接头拉伸性能及断裂特征的影响[J]. 机械工程学报, 2015, 51(22): 29-34.
[14]	王志平;程涛涛;丁坤英. 颗粒致密度对WC-10Co-4Cr涂层性能的影响[J]. , 2011, 47(24): 63-68.