基于旁路耦合电弧的铝钢MIG熔钎焊研究

›› 2011, Vol. 47 ›› Issue (16): 25-29.

基于旁路耦合电弧的铝钢MIG熔钎焊研究

石玗;温俊霞;黄健康;卢立晖;樊丁;张裕明

兰州理工大学甘肃省有色金属新材料重点实验室;兰州理工大学有色金属合金及加工教育部重点实验室;肯塔基大学制造中心

发布日期:2011-08-20

Study on DE-GMAW MIG-brazing Method for Bonding Steel with Aluminum

SHI Yu;WEN Junxia;HUANG Jiankang;LU Lihui;FAN Ding;ZHANG Yuming

State Key Laboratory of Gansu Advanced Nonferrous Metal Materials, Lanzhou University of Technology Key Laboratory of Nonferrous Metal Alloys of Ministry of Education, Lanzhou University of Technology Center for Manufacturing, University of Kentucky

Published:2011-08-20

摘要/Abstract

摘要： 实现铝钢良好连接的关键是有效控制焊接热输入，尽量降低中间层铝铁金属间化合物的厚度，一般认为中间层金属间化合物厚度小于10 μm时铝钢接头质量良好。提出旁路耦合电弧熔钎焊方法，通过调节旁路电弧电流的大小来控制焊接热输入。在优化控制系统和工艺参数的基础上采用脉冲旁路耦合电弧焊方法将铝镁合金ER5356堆焊到304不锈钢板上，获得结合良好的焊缝。对焊接接头进行扫描电镜(Scanning electron microscope, SEM)、能量色散光谱仪(Energy dispersive spectrometry, EDS)分析，结果表明：铝与不锈钢焊接接头中间层金属间化合物平均厚度约为8 μm，小于10 μm的临界厚度；脉冲旁路耦合电弧焊方法能够实现铝钢的连接，是一种新型低成本低热输入电弧焊方法。

关键词: 铝/钢异种金属焊接, 旁路耦合电弧焊, 熔钎焊

Abstract: Hhe key of welding aluminum to steel is accurate control of heat input, aiming at reducing the brittle inter-metallic compound (IMC) in the interfacial layer. A novel gas metal arc welding (GMAW) process, referred to as double-electrode GMAW, is developed to make it possible to increase the wire melting current while the base metal current is still controlled at a desired level. To accurately control the heat-input, pulse double-electrode GMAW experiments are carried out to joint aluminum wire ER5356 to 304 steel on the basis of optimizing control system and welding parameters. Analysis on the welding joint by means of scanning electron microscope(SEM) and energy dispersive spectrometry (EDS) shows that the IMC layer is less than 10 μm，which is the generally accepted critical thickness. Pulse Bypass-Electrode GMAW, being one of economic low heat-input arc welding methods, is feasible for welding aluminum to steel.

Key words: Dissimilar metals welding of aluminum and steel, Double-electrode gas metal arc welding(DE-GMAW), MIG-brazing

中图分类号:

TG434

石玗;温俊霞;黄健康;卢立晖;樊丁;张裕明. 基于旁路耦合电弧的铝钢MIG熔钎焊研究[J]. , 2011, 47(16): 25-29.

SHI Yu;WEN Junxia;HUANG Jiankang;LU Lihui;FAN Ding;ZHANG Yuming. Study on DE-GMAW MIG-brazing Method for Bonding Steel with Aluminum[J]. , 2011, 47(16): 25-29.

[1]	秦国梁, 武传松. 铝合金/钢异种材料熔钎焊接工艺及其研究现状^*[J]. 机械工程学报, 2016, 52(24): 24-35.
[2]	李永兵, 马运五, 楼铭, 雷海洋, 林忠钦. 轻量化多材料汽车车身连接技术进展^*[J]. 机械工程学报, 2016, 52(24): 1-23.
[3]	李春玲, 樊丁, 王斌, 黄健康. 电弧辅助铝/镀锌钢涂粉激光熔钎焊界面特性与性能[J]. 机械工程学报, 2015, 51(18): 57-63.
[4]	黄健康, 何笑英, 张正鹏, 沈利民, 石玗, 樊丁. 脉冲DE-GMAW过程熔滴受力分析及电流波形设计研究[J]. 机械工程学报, 2015, 51(14): 72-77.
[5]	余淑荣;蒋锴;樊丁. 5056铝合金/镀锌钢预置涂粉激光熔钎焊组织及性能研究[J]. , 2014, 50(12): 83-88.
[6]	黄健康;韩日宏;石玗;樊丁;张裕明. 双旁路耦合电弧MIG焊熔滴过渡受力分析[J]. , 2012, 48(8): 44-48.