陶瓷磨削表面变质层的产生机理

›› 2000, Vol. 36 ›› Issue (11): 30-32.

陶瓷磨削表面变质层的产生机理

田欣利;徐燕申;彭泽民;林彬

装甲兵工程学院材料系;天津大学

发布日期:2000-11-15

GENERATING MECHANICAL OF SURFACE DEGENERATING LAYER ON CERAMIC GRINDING

Tian Xinli;Xu Yanshen;Peng Zemin;Lin Bin

Armored Force Engineering Institute Tianjin University

Published:2000-11-15

摘要/Abstract

摘要： 研究了陶瓷磨削表面变质层的产生机理。经扫描电镜观察发现了磨削表面非晶层的粘性行为和匀质化过程。采用物相分析和X射线衍射谱线分析证实了变质层中微晶的存在，通过能谱分析确定了非晶层的化学成分，在对玻璃相结构分析的基础上研究证实了Al 2O 3陶瓷表面变质层是由碎（微）晶和玻璃态化合物组成的塑性层，并解释了表面晶粒的碎化机理。

关键词: 表面变质层, 产生机理, 陶瓷磨削

Abstract: The generating mechanism of grinding surface degenerating layer of the ceramics is studied. Sticky behavior and even process of the surface degenerating layer are discovered by SEM. The presence of micro-crystals in the degenerating layer is verified by the method of phase analysis and X-ray diffraction . The chemical composition of the layer is determined by energy spectrum. On the basis of the analysis of the glassiness structure, it is proved that the surface degenerating layers is made up of fragmental crystals or micro-crystals and glassiness compound. The caused of crystal fragmentation is explained.

Key words: Ceramic grinding, Generating mechanism, Surface degenerating layer

中图分类号:

TH16

田欣利;徐燕申;彭泽民;林彬. 陶瓷磨削表面变质层的产生机理[J]. , 2000, 36(11): 30-32.

Tian Xinli;Xu Yanshen;Peng Zemin;Lin Bin. GENERATING MECHANICAL OF SURFACE DEGENERATING LAYER ON CERAMIC GRINDING[J]. , 2000, 36(11): 30-32.