Study on Strengthening Mechanism and Anti-fatigue Performance of Stress Ultrasonic Rolling

doi:10.3901/JME.2024.09.127

Abstract

Abstract: The basic principle of coupling ultrasonic rolling with uniaxial tensile elastic stress field is discussed from the perspective of theoretical analysis, and the results of theoretical analysis are verified from the perspective of numerical simulation and experiment through finite element simulation and experimental characterization in turn. Thus, a new advanced surface mechanical strengthening process, stress ultrasonic rolling, is developed and successfully applied to enhance the surface mechanical strengthening effect and fatigue resistance of TiB2/2024 and TiB2/7050 aluminum matrix composites. Compared with ultrasonic rolling, the results showed that, after stress ultrasonic rolling, the peak compressive residual stresses in the surface layers of TiB2/2024 and TiB2/7050 aluminum matrix composites are increased by 45% and 70% of the applied uniaxial tensile elastic stress values, respectively, the depth of the layer affected by compressive residual stresses is increased by about 100 μm, and the fatigue limits of the two composite samples were further increased by 6% and 5%, respectively.

Key words: stress ultrasonic rolling, aluminum matrix composites, finite element simulation, experimental characterization, fatigue

CLC Number:

TG156

WU Jie, DANG Jiaqiang, LI Yugang, CHEN Dong, AN Qinglong, WANG Haowei, CHEN Ming. Study on Strengthening Mechanism and Anti-fatigue Performance of Stress Ultrasonic Rolling[J]. Journal of Mechanical Engineering, 2024, 60(9): 127-136.

Add to citation manager EndNote|Reference Manager|ProCite|BibTeX|RefWorks

URL: http://www.cjmenet.com.cn/EN/10.3901/JME.2024.09.127

http://www.cjmenet.com.cn/EN/Y2024/V60/I9/127

References

[1] 朱有利，王燕礼，边飞龙，等. 金属材料超声表面强化技术的研究与应用进展[J]. 机械工程学报，2014，50(20)：35-45. ZHU Youli，WANG Yanli，BIAN Feilong，et al. Progresses on research and application of metal ultrasonic surface enhancement technologies [J]. Journal of Mechanical Engineering，2014，50(20)：35-45.
[2] YE Y，Kure-Chu S Z，SUN Z，et al. Nanocrystallization and enhanced surface mechanical properties of commercial pure titanium by electropulsing-assisted ultrasonic surface rolling [J]. Materials & Design，2018，149：214-227.
[3] Wang H，Song G，Tang G. Enhanced surface properties of austenitic stainless steel by electropulsing-assisted ultrasonic surface rolling process [J]. Surface and Coatings Technology，2015，282：149-154.
[4] Ji R，Liu Y，To S，et al. Efficient fabrication of gradient nanostructure layer on surface of commercial pure copper by coupling electric pulse and ultrasonics treatment [J]. Journal of Alloys and Compounds，2018，764：51-61.
[5] Xie J，Zhang S，Sun Y，et al. Microstructure and mechanical properties of high entropy CrMnFeCoNi alloy processed by electopulsing-assisted ultrasonic surface rolling [J]. Materials Science and Engineering：A，2020，795：140004.
[6] Wang Z，Liu Z，Gao C，et al. Modified wear behavior of selective laser melted Ti6Al4V alloy by direct current assisted ultrasonic surface rolling process [J]. Surface and Coatings Technology，2020，381：125122.
[7] Liu J，Suslov S，Vellore A，et al. Surface nanocrystallization by ultrasonic nano-crystal surface modification and its effect on gas nitriding of Ti6Al4V alloy [J]. Materials Science and Engineering：A，2018，736：335-343.
[8] Ye H，Sun X，Liu Y，et al. Effect of ultrasonic surface rolling process on mechanical properties and corrosion resistance of AZ31B Mg alloy [J]. Surface and Coatings Technology，2019，372：288-298.
[9] 栾晓圣，梁志强，赵文祥，等. 超高强度钢热场-超声复合滚压表层微观组织强化机制[J]. 机械工程学报，2023，59(4)：34-42. LUAN Xiaosheng，LIANG Zhiqiang，ZHAO Wenxiang，et al. Microstructure strengthening mechanism of surface layer of ultra-high strength steel by thermal assisted ultrasonic rolling [J]. Journal of Mechanical Engineering，2023，59(4)：34-42.
[10] Xu X，Liu D，Zhang X，et al. Mechanical and corrosion fatigue behaviors of gradient structured 7B50-T7751 aluminum alloy processed via ultrasonic surface rolling [J]. Journal of Materials Science & Technology，2020，40：88-98.
[11] Xu X，Liu D，Zhang X，et al. Influence of ultrasonic rolling on surface integrity and corrosion fatigue behavior of 7B50-T7751 aluminum alloy [J]. International Journal of Fatigue，2019，125：237-248.
[12] Curtis S，De Los Rios E R，Rodopoulos C A，et al. Analysis of the effects of controlled shot peening on fatigue damage of high strength aluminium alloys [J]. International Journal of Fatigue，2003，25(1)：59-66.
[13] Li Y，Lian G，Geng J，et al. Effects of ultrasonic rolling on the surface integrity of in-situ TiB2/2024Al composite [J]. Journal of Materials Processing Technology，2021，293：117068.
[14] PrevÉy P S. The effect of cold work on the thermal stability of residual compression in surface enhanced IN718 [J]. 2000，426-434.
[15] Zhan K，Jiang C H，Ji V. Effect of prestress state on surface layer characteristic of S30432 austenitic stainless steel in shot peening process [J]. Materials & Design，2012，42：89-93.
[16] Hu Y，Li Z，Yu X，et al. Effect of elastic prestress on the laser peen forming of aluminum alloy 2024-T351：Experiments and eigenstrain-based modeling [J]. Journal of Materials Processing Technology，2015，221：214-224.
[17] Feng Q，Jiang C，Xu Z. Surface layer investigation of duplex stainless steel S32205 after stress peening utilizing X-ray diffraction [J]. Materials & Design，2013，47：68-73.
[18] Zhu K，Jiang C，Ji V. Surface layer characteristics of CNT/Al–Mg–Si alloy composites treated by stress peening [J]. Surface and Coatings Technology，2017，317：10-16.
[19] Huang J，Wang Z，Gan J，et al. Investigation of fatigue performance improvement in SiCw/Al composites with different modified shot peening treatments by considering surface mechanical properties [J]. Journal of Alloys and Compounds，2017，728：169-178.
[20] Schwab K-C，Keller S，Kashaev N，et al. Tailoring of residual stresses by specific use of defined prestress during laser shock peening [J]. Journal of Materials Processing Technology，2021，295：117154.
[21] Collin J-M，Parenteau T，Mauvoisin G，et al. Material parameters identification using experimental continuous spherical indentation for cyclic hardening [J]. Computational Materials Science，2009，46(2)：333-338.
[22] Chaboche J L. Time-independent constitutive theories for cyclic plasticity [J]. International Journal of Plasticity，1986，2(2)：149-188.
[23] ISO-1143：2010. Metallic materials-Rotating bar bending fatigue testing[M]. Geneve：International Organization for Standardization，2010.
[24] GB/T4337-2015. 金属材料-疲劳试验-旋转弯曲方法[M]. 北京：中华人民共和国国家质量监督检验检疫总局，中国国家标准化管理委员会，2015. GB/T4337-2015. Metallic materials-rotating bar bending fatigue testing [M]. Beijing：General Administration of Quality Supervision，Inspection and Quarantine of the People's Republic of China. 2015.
[25] ASTM-E915-10. Standard practice for verifying the alignment of X-Ray diffraction instruments for residual stress measurement[M]. WestConshohocken，PA：ASTM International，2010.
[26] EN-15305：2008. Non-destructive testing-Test method for residual stress analysis by X-ray diffraction[M]. Strasbourg：European Standard，2009.
[27] GB/T7704-2017. 无损检测-X射线应力测定方法[M]. 北京：中华人民共和国国家质量监督检验检疫总局，中国国家标准化管理委员会，2017. GB/T7704-2017. Non-destructive testing - Test method for stress analysis by X-ray diffraction [M]. Beijing：General Administration of Quality Supervision，Inspection and Quarantine of the People's Republic of China. 2017.
[28] 肖志瑜，叶旋，陆宇衡，等. 喷丸表面强化处理Fe-2Cu-2Ni-1Mo-1C材料的弯曲疲劳性能及断口分析[J]. 机械工程学报，2013，49(20)：152-157. XIAO Zhiyu，YE Xuan，LU Yuheng，et al. Effect of shot peening on bending fatigue strength and fractograph of Fe-Cu-Ni-Mo-C [J]. Journal of Mechanical Engineering，2013，49(20)：152-157.