Impact Damage Behavior of the Cemented Carbide Insert in the Heavy Cutting Process

doi:10.3901/JME.2014.23.175

Abstract

Abstract: Impact fracture process of cemented carbide turning tool is analyzed by using mechanics impact theory and the critical condition is also determined when the impact fracture happened. Finite element simulation is used to analyze and research production mechanism and damage form of impact fracture of cemented carbide turning tool, and through impact experiment the impact fracture rules of cemented carbide turning tool is revealed. The fatigue behavior of cemented carbide turning tool is researched, and through finite element simulation, production mechanism of fatigue fracture of cemented carbide under dynamic load is put forward, and the load condition of fatigue fracture of cemented carbide is given. Through intermittent cutting experiment, the essential reason why cemented carbide produced fatigue behavior is analyzed. All above will provide theory support and reference to prevent cemented carbide tool from failure too early.

Key words: carbide turning tool, cracks, fatigue fracture, heavy cutting, impact fracture

CLC Number:

TG712

LIU Xianli;LIU Ming;HE Genghuang;YAN Fugang;CHENG Yaonan;LIU Li. Impact Damage Behavior of the Cemented Carbide Insert in the Heavy Cutting Process[J]. , 2014, 50(23): 175-185.

Add to citation manager EndNote|Reference Manager|ProCite|BibTeX|RefWorks

URL: http://www.cjmenet.com.cn/EN/10.3901/JME.2014.23.175

http://www.cjmenet.com.cn/EN/Y2014/V50/I23/175

[1]	LIU Hongxia, WANG Xiaoxiao, CUI Yuanyuan, LIU Fang, YANG Jie, CHEN Haofeng. New Coalescence Criterion for Non-collinear Parallel Double Cracks [J]. Journal of Mechanical Engineering, 2025, 61(24): 148-157.
[2]	LIN Qiang, LIU Xing, TIAN Haidong, WANG Wenjian, DING Haohao, LIU Qiyue, GUO Jun. Research on the Influence Law of Size and Shape of Rail Crack on Alternating Current Field Measurement Signal [J]. Journal of Mechanical Engineering, 2025, 61(18): 38-49.
[3]	DONG Qingbing, CHEN Zhuang, LUO Zhentao, ZHANG Jie, WEI Jing. Fatigue Life Prediction and Fracture Behavior Study of Fretting Interface at Three-dimensional Line Contact [J]. Journal of Mechanical Engineering, 2024, 60(8): 107-120.
[4]	DU Kaikai, BAO Chen, HE Guangwei. Method to Evaluate Fatigue Crack Growth Rate of Semi-elliptical Surface Cracked Plates Under Bending [J]. Journal of Mechanical Engineering, 2024, 60(24): 153-162.
[5]	LEI Zhen, JIANG Hong, ZHANG Xiangfeng, LI Jun, KONG Yiyi, BAI Yu. Evolutionary Analysis of Tooth Cracks in Planetary Gear Systems [J]. Journal of Mechanical Engineering, 2024, 60(19): 101-115.
[6]	BI Siyuan, ZHANG Xinrui, LEI Zhenglong, LI Bingwei, XIA Peiyun. Influence of Beam Swing Mode on Cracks of Double-sided Laser Welding of 2195 Aluminum-lithium Alloy T-joint [J]. Journal of Mechanical Engineering, 2023, 59(22): 245-253.
[7]	XIE Yong, WANG Xiaonan, ZHOU Xiang, LIU Zhenguang, YAO Jun, DU Baorui, BAO Chengren. Research Progress of Grain Boundary Liquid Metal Embrittlement Cracks in Galvanized Ultra-high Strength Automotive Steel Resistance Spot Welded Joints [J]. Journal of Mechanical Engineering, 2023, 59(2): 39-50.
[8]	QI Lei, FEI Jiawen, WEN Jianfeng, TU Shantung. Interaction Behavior and Combination Rules of Two Through-wall Cracks under Tensile Loading [J]. Journal of Mechanical Engineering, 2023, 59(2): 113-126.
[9]	DAI Jianbo, SU Honghua, WANG Zhongbin, DING Wenfeng, FU Yucan, CHEN Jiajia. Research on the Crack Damage Formation Mechanisms of Polycrystalline Silicon Carbide Ceramics in Grinding Process [J]. Journal of Mechanical Engineering, 2022, 58(13): 307-320.
[10]	YIN Minxuan, ZHU Tao, YANG Bing, XU Jingtao, WANG Chao, XIAO Shoune. Fatigue Fracture Life of Heavy-haul Wagon’s CouplerKnuckle Based on Reliability [J]. Journal of Mechanical Engineering, 2021, 57(4): 210-218.
[11]	YAN Yan, LIU Yi, ZHU Junzhen, MIAO Ling, CHEN Xiaotian, ZHOU Yu, LU Yanping, GAO Bin, TIAN Guiyun. Quantification of Rolling Contact Fatigue Cracks in Rails Based on Eddy Current Pulsed Thermography with Skewness Feature [J]. Journal of Mechanical Engineering, 2021, 57(18): 75-85.
[12]	ZHANG Ting, CHEN Jie. Research on Phased Array Ultrasonic Testing Method for Titanium Alloy Sheet Fillet Welds [J]. Journal of Mechanical Engineering, 2021, 57(12): 145-152.
[13]	YANGYi, DANG Mingzhu, LI Wei, WEI Qingsong. Study on Cracking Mechanism and Inhibiting Process of TiAl Alloys Fabricated by Selective Laser Melting [J]. Journal of Mechanical Engineering, 2020, 56(3): 181-188.
[14]	JIN Qiaoling, WANG Haidou, LI Guolu, ZHANG Jianjun, LIU Jinna. Effect of Sputtering Power on the Mechanical Properties of Ti Film Based on the Nano Indentation Method and Nano Impact Method [J]. Journal of Mechanical Engineering, 2018, 54(2): 117-124.
[15]	YANG Jianguo, HAO Jiansong, LI Yuebing, ZHENG Wenjian, GAO Zengliang, ZHANG Pengcheng. Quality Category Approach of Fatigue Assessment for Welded Structures with Surface Cracks [J]. Journal of Mechanical Engineering, 2018, 54(14): 82-89.

Impact Damage Behavior of the Cemented Carbide Insert in the Heavy Cutting Process

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments