疲劳门槛值统一理论模型的比较及验证

doi:10.3901/JME.2020.24.081

机械工程学报 ›› 2020, Vol. 56 ›› Issue (24): 81-87.doi: 10.3901/JME.2020.24.081

扫码分享

疲劳门槛值统一理论模型的比较及验证

沈学成, 黄毓晖, 朱明亮, 轩福贞

华东理工大学机械与动力工程学院上海 200237

收稿日期:2020-05-20 修回日期:2020-09-05 出版日期:2020-12-20 发布日期:2021-02-05
通讯作者: 朱明亮(通信作者),男,1984年出生,教授。主要研究方向为机械结构疲劳与断裂。E-mail:mlzhu@ecust.edu.cn
作者简介:沈学成,男,1994年出生。主要研究方向为焊接结构的疲劳与断裂。E-mail:18721366832@163.com
基金资助:
国家自然科学基金资助项目（51922041）。

Comparison and Verification of Unified Fatigue Threshold Models

SHEN Xuecheng, HUANG Yuhui, ZHU Mingliang, XUAN Fuzhen

School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237

Received:2020-05-20 Revised:2020-09-05 Online:2020-12-20 Published:2021-02-05

摘要/Abstract

摘要： 针对应力比对疲劳裂纹扩展及门槛值的影响，依据裂纹闭合与裂纹扩展驱动力机制的统一思想，阐述了Zhu-Xuan模型与Kwofie-Zhu模型的建立过程，并基于25Cr2Ni2MoV转子钢焊接接头的疲劳裂纹扩展试验数据对模型进行验证。结果表明，两种模型在近门槛值区和Paris区均有良好的预测效果，其中Zhu-Xuan模型形式简单，对CrMoV钢具有普适性，预测门槛值的误差在10%以内，而Kwofie-Zhu模型预测结果更准确，但应用过程涉及参数求解，过程较复杂。研究认为，裂纹闭合与扩展驱动力机制的统一模型描述疲劳裂纹扩展行为的应力比相关性是合理可行的，且具有较好精度。

关键词: 疲劳裂纹扩展, 应力比, 疲劳门槛值, 裂纹闭合, 裂纹扩展驱动力

Abstract: Aiming at the effect of stress ratio on fatigue crack growth and fatigue threshold, the establishment process of Zhu-Xuan model and Kwofie-Zhu model are described, based on the unified thought of crack closure and crack propagation driving force mechanism, and the models are verified by using fatigue crack growth data of 25Cr2Ni2MoV rotor steel welded joint. Results show that both the two models can well predict fatigue cracking in the near threshold and Paris regimes. The Zhu-Xuan model has a simpler form and is universal for CrMoV steel with an error of fatigue threshold prediction below 10%, while the prediction by the Kwofie-Zhu model is more accurate, and the application involves parameter solving, and is thus more complicated. It is demonstrated that the unified mechanistic modeling of crack closure and crack growth driving force to describe stress ratio dependence of fatigue crack growth behavior is reasonable and feasible with good accuracy.

Key words: fatigue crack growth, stress ratio, fatigue threshold, crack closure, crack growth driving force

中图分类号:

TG115

沈学成, 黄毓晖, 朱明亮, 轩福贞. 疲劳门槛值统一理论模型的比较及验证[J]. 机械工程学报, 2020, 56(24): 81-87.

SHEN Xuecheng, HUANG Yuhui, ZHU Mingliang, XUAN Fuzhen. Comparison and Verification of Unified Fatigue Threshold Models[J]. Journal of Mechanical Engineering, 2020, 56(24): 81-87.

参考文献

[1] MADDOX S J. The effect of mean stress on fatigue crack propagation a literature review[J]. International Journal of Fracture,1975,11(3):389-408.
[2] 杜彦楠,朱明亮,轩福贞. 应力比对25Cr2Ni2MoV钢焊接接头近门槛值区疲劳裂纹扩展曲线转折点的影响[J]. 机械工程学报,2015,51(8):44-49. DU Yannan,ZHU Mingliang,XUAN Fuzhen. Effect of stress ratio on the transition point of fatigue crack growth curve in the near-threshold regime of a 25Cr2Ni2MoV steel welded joint[J]. Journal of Mechanical Engineering. 2015,51(8):44-49.
[3] RITCHIE R O,SURESH S. Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphology[J]. Metallurgical Transactions A,1982,13(5):937-940.
[4] MCEVILY A J,RITCHIE R O. Crack closure and the fatigue-crack propagation threshold as a function of load ratio[J]. Fatigue & Fracture of Engineering Materials & Structures,1998,21(7):847-855.
[5] ELBER W. The significance of fatigue crack closure[C]//Proceedings of the Damage Tolerance in Aircraft Structures,Canada,1970. ASTM STP 486:230-242.
[6] WALKER K. The effect of stress ratio during crack propagation and fatigue for 2024-T3 and 7075-T6 aluminum[C]//Proceedings of the Effects of environment and complex load history on fatigue life:A Symposium,Lutherville-Timonium,MD,1970. ASTM STP 462:1-14.
[7] KWOFIE S,RAHBAR N. An equivalent driving force model for crack growth prediction under different stress ratios[J]. International Journal of Fatigue,2011,33(9):1199-1204.
[8] ZHU M L,XUAN F Z,TU S T. Interpreting load ratio dependence of near-threshold fatigue crack growth by a new crack closure model[J]. International Journal of Pressure Vessels and Piping,2013,110:9-13.
[9] ZHU M L,XUAN F Z,TU S T. Effect of load ratio on fatigue crack growth in the near-threshold regime:A literature review,and a combined crack closure and driving force approach[J]. Engineering Fracture Mechanics,2015,141:57-77.
[10] DU Y N,ZHU M L,LIU X,et al. Effect of long-term aging on near-threshold fatigue crack growth of Ni-Cr-Mo-V steel welds[J]. Journal of Materials Processing Technology,2015,226:228-237.
[11] KWOFIE S,ZHU M L. Modeling R-dependence of near-threshold fatigue crack growth by combining crack closure and exponential mean stress model[J]. International Journal of Fatigue,2019,122:93-105.
[12] CHAN K S. Variability of large-crack fatigue-crack-growth thresholds in structural alloys[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,2004,35A(12):3721-3735.

[1]	王博士, 陈楠楠, 蔡艳, 王敏. 低合金贝氏体高强钢模拟焊接粗晶热影响区低温疲劳韧脆转变行为及机制[J]. 机械工程学报, 2024, 60(6): 271-278.
[2]	高冲, 董丽虹, 王海斗, 刘彬, 吕晓仁. 整体加筋结构疲劳损伤研究进展[J]. 机械工程学报, 2024, 60(18): 116-127.
[3]	喻健, 缑百勇, 陈桂勇, 张腾, 马斌麟, 樊祥洪, 陈鑫, 王逸韬. 胶铆混合修理结构疲劳裂纹扩展性能分析[J]. 机械工程学报, 2023, 59(22): 352-368.
[4]	李鹤飞, 张鹏, 张哲峰. 高强钢断裂韧性与疲劳裂纹扩展评价方法研究进展[J]. 机械工程学报, 2023, 59(16): 18-31.
[5]	王超, 杨冰, 朱涛, 肖守讷, 阳光武, 范晓达. 表面强化车轴裂纹扩展及剩余寿命预测方法研究[J]. 机械工程学报, 2023, 59(14): 43-53.
[6]	马硕, 姜兴宇, 杨国哲, 刘伟军, 乔赫廷, 王子生. 废旧机床主轴剩余寿命评估模型[J]. 机械工程学报, 2021, 57(4): 219-226.
[7]	江荣, 吴常皓, 万煜伟, 张禄, 宋迎东. 涡轮盘合金氧化-疲劳裂纹扩展机理和寿命预测研究进展[J]. 机械工程学报, 2021, 57(16): 122-131.
[8]	杨冰, 魏占江, 廖贞, 肖守讷, 阳光武, 朱涛, 王明猛, 邓永权. 单峰过载对工业纯钛CT试样裂纹闭合效应的影响[J]. 机械工程学报, 2021, 57(12): 169-178.
[9]	吴圣川, 谢成, 胡雅楠, 吴正凯, 康国政. 中高强度铝合金熔化焊接接头的缺陷容限评价方法[J]. 机械工程学报, 2020, 56(8): 46-59.
[10]	祁爽, 蔡力勋, 包陈, 刘晓坤. 30Cr2Ni4MoV转子钢II型裂纹的疲劳扩展行为[J]. 机械工程学报, 2020, 56(20): 88-97.
[11]	高红俐, 郑欢斌, 朱亚伦. 裂纹扩展过程中电磁谐振疲劳试验系统动态特性分析^*[J]. 机械工程学报, 2016, 52(24): 88-98.
[12]	上官文斌, 王小莉, 段小成, 刘国兵, 阎礁. 变幅载荷下隔振器橡胶材料裂纹扩展试验及建模方法[J]. 机械工程学报, 2015, 51(8): 50-58.
[13]	杜彦楠, 朱明亮, 轩福贞. 应力比对25Cr2Ni2MoV钢焊接接头近门槛值区疲劳裂纹扩展曲线转折点的影响[J]. 机械工程学报, 2015, 51(8): 44-49.
[14]	李煜佳, 轩福贞, 涂善东. 应力比和残余应力对Ti-6Al-4V高周疲劳断裂模式的影响[J]. 机械工程学报, 2015, 51(6): 45-50.
[15]	华亮1, 2, 田威3, 廖文和1, 曾超3. 基于非线性连续疲劳损伤的再制造毛坯剩余寿命评估[J]. 机械工程学报, 2015, 51(21): 132-136.

疲劳门槛值统一理论模型的比较及验证

Comparison and Verification of Unified Fatigue Threshold Models

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价