固溶处理对7B04-O铝合金搅拌摩擦焊接接头微观组织与力学性能的影响

韩培培1,  杨 超2,  王继杰2,  杜宝瑞1,  刘晓寒1,  薛鹏3,  马宗义3,  倪丁瑞3   

  1. 1. 中航工业沈阳飞机工业(集团)有限公司  沈阳  110850;
    2. 沈阳航空航天大学材料科学与工程学院  沈阳  110036;
    3. 中国科学院金属研究所沈阳材料科学国家(联合)实验室  沈阳  110016
  • 收稿日期:2015-03-25 修回日期:2015-06-24 出版日期:2015-11-15 发布日期:2015-11-15
  • 通讯作者: 倪丁瑞,男,1976年出生,博士,副研究员。主要研究方向为搅拌摩擦焊接与加工。 E-mail:drni@imr.ac.cn
  • 作者简介:作者简介:韩培培,女,1983年出生,工程师。主要研究方向为搅拌摩擦焊和热处理技术。 E-mail:hanpp1983@126.com
  • 基金资助:
    国家自然科学基金资助项目(51331008)

Effects of Solution Heat Treatment on Friction Stir Welding Joints of 7B04-O Aluminum Alloy

HAN Peipei1,  YANG Chao2,  WANG Jijie2,  DU Baorui1,  LIU Xiaohan1, XUE Peng3,  MA Zongyi3,  NI Dingrui3   

  1. 1. AVIC Shenyang Aircraft Corporation, Shenyang 110850;
    2. College of Material Science and Engineering, Shenyang Aerospace University, Shenyang 110036;
    3. Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
  • Received:2015-03-25 Revised:2015-06-24 Online:2015-11-15 Published:2015-11-15

摘要: 对航空用3 mm厚的带有包铝层的7B04-O铝合金板材进行搅拌摩擦焊接(Friction stir welding,FSW),研究固溶处理对搅拌摩擦焊接接头的微观组织和力学性能的影响。结果表明,当转速为800 r/min、焊接速度为200 mm/min、焊接工具轴肩直径为12 mm时,可得到表面美观、致密无缺陷的搅拌摩擦焊接接头。焊核区发生动态再结晶,形成细小的等轴晶。经固溶处理后,焊核的上部及底部晶粒都发生了异常长大,而中部区域晶粒仍然为细小的等轴晶组织。焊态接头的拉伸试样断裂在母材位置,抗拉强度达到199 MPa,与退火态母材抗拉强度相当,断后伸长率达到12%。在新淬火状态下,接头的抗拉强度为310 MPa,为相同热处理母材的91.4%,断后伸长率为11.2%,试样断裂在焊核区,呈不完全的韧性断裂。

关键词: 7B04铝合金, 搅拌摩擦焊, 力学性能, 热处理, 微观组织

Abstract: The aero Al-coating 7B04-O aluminum alloy plates with the thickness of 3 mm are subjected to friction stir welding (FSW), the effect of solution heat treatment on the microstructure and tensile property of the FSW joints are investigated. The results show that, with the rotation rate of 800 r/min, the welding speed of 200 mm/min and the shoulder diameter of 12 mm, sound FSW joints with no defect are obtained. Dynamic recrystallization take place in the nugget zones(NZs) with fine and equiaxed grains generated. After the heat treatment, the abnormal growth of grain is found in both the upper and the bottom parts of the NZs, whereas the fine equiaxed grains in the center part is retained. During the tensile test, the fraction position occurs in the base metal of the welded joint. The ultimate tensile strength of the welded joint is 198 MPa, which is equal to that of the base metal. the breaking elongation is about 13.2%. After the solution heat treatment, the tensile strength and breaking elongation of the FSW joint are about 310 MPa and 11.2% respectively, and the joint fails in the NZ during the tensile test, which shows incomplete ductile fracture.

Key words: 7B04 aluminum alloy, friction stir welding, heat treatment, mechanical property, microstructure